中文摘要：
将高铁一水硬铝石矿进行马弗炉、强磁场焙烧预处理，分别考察焙烧温度和磁场强度对焙烧矿溶出赤泥沉降性能的影响；利用XRD对焙烧矿溶出赤泥的物相组成变化进行分析，并进一步探讨焙烧矿赤泥沉降眭能变化机理。结果表明：焙烧预处理对矿物的沉降性能有较大影响，马弗炉焙烧预处理条件为焙烧温度550℃、保温时间60min；强磁场焙烧预处理条件为磁场强度9T、500℃、60min；预处理后的焙烧矿赤泥的沉降性能均较原矿有所提高，且强磁场焙烧矿赤泥的沉降性能优于马弗炉焙烧矿的。
英文摘要：
The diasporic bauxite with high-iron content was pre-roasted in muffle furnace and strong magnetic field, respectively, to investigate the effects of roasting temperature and magnetic field intensity on the settling performance of red mud from roasted diasporic bauxite. The changes of phase composition of the diasporic bauxite with high-iron content were analyzed by XRD, and the change mechanism of the settling performance of the red mud was discussed. The results indicate that pre-roasting has considerable effect on the settling performance of the ore. The suitable pre-roasting conditions by using muffle furnace and strong magnetic field are 550 ℃ for 60 min and 500 ℃ for 60 min in 9 T, respectively. Under these conditions, the settling performance of red mud is improved. The settling performance of the red mud treated in the strong magnetic field is better than that of red mud treated in muffle furnace.
同期刊论文项目
同项目期刊论文
Study on the leaching rules of aluminum and ferrum from high iron bauxite by acid leaching at low te
期刊信息
位置：