中文摘要：
采用球磨、喷雾干燥、气流粉碎三种方法分别对酶解木质素（EHL）进行预处理，考察其对丁腈橡胶（NBR）的补强性能影响。结果表明，EHL经气流粉碎预处理后的堆积密度最小（O3329g．cm^-3），其在NBR基质中的分散粒径最细（约为25μm）且最均匀，对NBR的补强效果也最好。硫化胶的综合力学性能方面，气流粉碎预处理方法明显优于球磨法和喷雾干燥法。当EHL的用量为40质量份（phr）时，气流粉碎的NBPUEHL硫化胶的拉伸强度比球磨法、喷雾干燥法分别高出24.44％、61.29％；比空白NBR的拉伸强度提高257％。热重及热氧老化力学性能分析表明，酶解木质素在NBPUEHL共混体系中起到一定的热稳定及抗老化作用。扫描电镜图像显示，气流粉碎的酶解木质素与NBR的相容性比球磨、喷雾干燥法的有较大提高，木质素颗粒与橡胶相间的相互作用力较强。
英文摘要：
The influence of three pretreatment methods （Ball Milling （BM）, Spray Drying （SD） and Jet Milling （JM）） of Enzymatic Hydrolysis Lignin （EHL） on their acrylonitrile butadiene rubber （NBR） reinforcement abilities was investigated. The results show that the Jet Milled Lignin （EHL-JM） has the smallest bulk density （0.3329 g.cm^-3）, the finest particle size （about 2.5 μm） and the best dispersion in NBR matrices, which results in the best strengthening effect. When 40 phr （parts per hundred rubber） lignin was added, the tensile strength of NBR reinforced by EHL-JM is 24.44% and 61.29% higher than that of EHL-BM and EHL-SD, respectively, and the tensile strength is 257% times higher than that of pure NBR. Thermogravimetry results and the analysis of thermal-oxidative aging mechanical properties reveal that EHL can enhance thermal-stabilizing and anti-aging properties of the NBR/EHL blends. Scanning electron microscope images show that, comparing with EHL-BM and EHL-SD, EHL-JM has better compatibility with NBR and the interphase adhesion between lignin particles and rubber is stronger.
同期刊论文项目
同项目期刊论文
Influence of modified lignosulfonate GCL4-1 with different molecular weight on the stability of dime
?Effect of the Interfacial Agents with Different Types of Hydrophilic Functional Groups on the Rheol
Development and evaluation of polycarboxylic acid hyper-dispersant used to prepare high-concentrated
Preparation and Evaluation of Carboxymethylated Lignin as Dispersant for Aqueous Graphite Suspension
Determination of absolute molecular weight of sodium lignosulfonates (NaLS) by laser light scatterin
pH-Induced Lignin Surface Modification to Reduce Nonspecific Cellulase Binding and Enhance Enzymatic
The adsorption and dispersing mechanism of sodium lignosulfonate on Al2O3 particles in aqueous solut
Preparation of Lignin-Based Superplasticizer by Graft Sulfonation and Investigation of the Dispersiv
Reducing non-productive adsorption of cellulase and enhancing enzymatic hydrolysis of lignocellulose
Evaluation of Steric Repulsive Force in the Aqueous Dispersion System of Dimethomorph Powder with Li
Solution behaviors and adsorption characteristics of sodium lignosulfonate under different pH condit
Adsorption of different molecular weight lignosulfonates on dimethomorph powder in an aqueous system
期刊信息
位置：