VO_2薄膜的制备及其热致相变特性研究
  • ISSN号:1001-9731
  • 期刊名称:《功能材料》
  • 时间:0
  • 分类:TQ135.1[化学工程—无机化工]
  • 作者机构:[1]四川大学材料科学与工程学院,四川成都610064
  • 相关基金:国家自然科学基金资助项目(61271075)
中文摘要:

以双氧水和V2O5粉末为前驱体制备出V2O5溶胶,然后在云母基底上成膜,通过后续热处理退火得到优异相变性能的VO2薄膜。采用SEM、XRD分析薄膜形貌和微观结构,利用FT-IR等检测薄膜的光学性质。实验表明,VO2薄膜在云母基底上沿(011)晶面择优取向生长,颗粒生长致密且大小分布均匀。薄膜具有优异的相变陡然性,相变温度及滞后温宽都较低。在红外波段,相变前后透过率及反射率变化都较大,对红外光调节性能较好;在可见光波段,薄膜在相变前后都具有较高可见光透过率。

英文摘要:

The mixture of hydrogen peroxide and vanadium pentaoxide powder was used as a precursor to prepare V2O5 sol on the muscovite substrate. Then the V2O5 film is annealed to fabricate the VO2 film. SEM, XRD were employed to analyze the morphology and microstructure of the film. FT-IR and UV-Vis spectrophotometer were used to test the optical properties. The result indicate that the film is perfectly (011) orientated on muscovite substrate. The grains are compact and the size distributed uniformly. The film has excellent MIT sharpness. The phase transition temperature and the hysteresis width are lower. In the infrared, the change of the transmittance and reflectance are larger. In visible, the thin film has high transmittance both before and after phase transition.

同期刊论文项目
同项目期刊论文
期刊信息
  • 《功能材料》
  • 北大核心期刊(2011版)
  • 主管单位:重庆材料研究院
  • 主办单位:重庆材料研究院
  • 主编:黄伯云
  • 地址:重庆北碚区蔡家工业园嘉德大道8号
  • 邮编:400707
  • 邮箱:gnclwb@126.com
  • 电话:023-68264739
  • 国际标准刊号:ISSN:1001-9731
  • 国内统一刊号:ISSN:50-1099/TH
  • 邮发代号:78-6
  • 获奖情况:
  • 2008、2011年连续获中国精品科技期刊,2010获重庆市双十佳期刊
  • 国内外数据库收录:
  • 美国化学文摘(网络版),荷兰文摘与引文数据库,美国工程索引,日本日本科学技术振兴机构数据库,中国中国科技核心期刊,中国北大核心期刊(2004版),中国北大核心期刊(2008版),中国北大核心期刊(2011版),中国北大核心期刊(2014版),英国英国皇家化学学会文摘,中国北大核心期刊(2000版)
  • 被引量:30166