中文摘要：
以Fe粉、NiO、ZnO 为原料,NaClO4为氧源,NaCl 为稀释剂,通过燃烧合成法成功制备了千克级超细NiZn铁氧体.采用XRD、SEM、EDS以及VSM等研究了 Fe 粉含量对 NiZn 铁氧体粉体相组成、形貌和磁性能的影响.结果表明,随着Fe粉含量k 增加,退火后颗粒尺寸逐渐增大,外形呈现为扁平球形,形成了单相铁氧体,最小粒径为750 nm,最大为1200 nm.当k＝0．7时退火的产物饱和磁化强度最大为66 A？m2/kg,而k＝0．5时产物的矫顽力最小可达16．29×79．6 A/m.
英文摘要：
NiZn ferrite ultrafine powder were prepared by combustion synthesis using Fe,NiO and ZnO as raw materials,NaClO4 as oxygen source and NaCl as diluent.The effects of Fe amount on phases,morphology and magnetic properties were systematically investigated using scanning electron microscopy （SEM）,X-ray diffrac-tion （XRD）,energy dispersive spectrometer （EDS）and vibrating sample magnetism （VSM）.The results showed that the size of annealed powders increased and size distribution became broader with the Fe content. After annealing,the crystalline structure of powders is more complete,the saturation magnetization of the powders reached its maximum value at 6 A-m2/kg when k is 0.7,while the coercivity obtain its minimum val-ue at 16.29×79.6 A/m when k is 0.5.
同期刊论文项目
同项目期刊论文
White cast iron with a nano-eutectic microstructure and high tensile strength and considerable ducti
EFFECTS OF Al ELEMENT ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF HOT-ROLLED 316L STAINLESS STEEL
Investigation of Nanomechanical Properties of beta-Si3N4 Thin Layers in a Prismatic Plane under Tens
Effect of chromium content on microstructure and mechanical properties of large dimensional bulk nan
Theoretical Research of Electronic Structures and Optical Properties of beta-Si-2[Si(1-x)Ybx]N-4 (x=
Research of electronic structures and optical properties of Na- and Mg-doped b-Si 3 N 4 based on the
Effect of annealing on microstructure and mechanical properties of large dimensional bulk nanocrysta
Effect of Mn element on microstructure and mechanical properties of bulk nanocrystalline Fe3Al based
Effects of Different Substrates on Microstructures and Mechanical Properties of a Bimodal Bulk Nano/
Effect of substrates on microstructure and mechanical properties of nano-eutectic 1080 steel produce
Effect of annealing temperature on microstructure and mechanical properties of bulk 316L stainless s
Microstructure and tensile properties of 304 stainless steel with different combination of dual nano
Reduced graphene oxide-coated cottons for selective absorption of organic solvents and oils from wat
Microstructures and tensile properties of 304 steel with dual nanocrystalline and microcrystalline a
Insight into the nanomechanical properties under indentation of beta-Si3N4 nano-thin layers in the b
期刊信息
位置：