中文摘要：

应用软包装技术，用S-C复合材料作为Li／S电池的正极材料，组装了软包装Li／S电池。性能测试结果表明：120mA首次放电容量达1700mAh，比能量达300Wh／kg；循环50次（100mA）后的容量保持率约为60％。在0℃和-20℃下的放电容量（100mA）分别达25℃下放电容量的90％和40％。电池在过充电和短路等滥用条件下，不燃烧、不爆炸。

英文摘要：

The soft-package Li/S battery with S-C composite material as cathode material was assembled by applying soft-package technology. The performance test results showed that the initial discharge capacity at 120 mA was 1 700 mAh, the specific energy was 300 Wh/kg, the capacity retention rate （ 100 mA） was about 60% after 50 cycles. The discharge capacity （ 100 mA） at 0 ℃ and - 20 ℃ retained 90% and 40% of that at 25℃. The battery would not burn or explode at overcharge and short circuit.