中文摘要：
采用XPS分析钢筋经模拟混凝土孔隙液浸泡后表面膜的化学组成，结合线性极化法和动电位扫描阳极极化曲线测试，研究钢筋在模拟混凝土孔隙液中表面膜化学组成与腐蚀电化学行为的关联．结果表明：钢筋在纯模拟液中处于钝化状态．在含Cl-和不同pH值的模拟混凝土孔隙液中，随着Cl-浓度的增加和pH值的降低，钢筋的腐蚀电位负移，电流密度增大；钢筋表面钝化膜Fe^2＋的含量增加，Fe^2＋的含量减少．当模拟液中外加C1-浓度达0．6mol／L或pH值降至11．31时，钢筋表面不发生钝化，但加入0．24mol／LNaNO2缓蚀剂后又可使钢筋钝化从而抑制腐蚀．
英文摘要：
It is well known that reinforcing steel in concrete can be protected from corrosion by forming a compact passive film on its surface in a concrete pore solution with high alkalinity. The corrosion behavior of the steel is related to its passivation and depassivation. The pH value and the C1- concentration in a concrete pore solution are of the most important parameters affecting the passivity of reinforcing steel in concrete. In the present work, XPS analysis, linear polarization and potentiodynamic anodic polarization tests were used to study the relationship between the electrochemical corrosion behavior of reinforcing steel immersed in a simulated concrete pore solution and the chemical composition of the steel surface film C1- concentration or the decrease of the pH value The results showed that with the increase of the in the solution, the corrosion potential of the steel shifted negatively and its corrosion current density rose, and the Fe^2＋ content of the steel surface film increased and the Fe^2＋ content decreased. The steel was in an active state in the solution with C1- concentration higher than 0.6 mol/L or pH lower than 11.31, and the addition of 0.24 mol/L NaNO2 to the solution could protect steel from corrosion.
同期刊论文项目
同项目期刊论文
The influence of Ce(NO3)3.6H2O on the of inhibitive Effect of Ca(NO2)2 IN Simulated Concrete Pore So
Corrosion behavior of steel in simulated concrete pore solutions treated with calcium silicate hydra
Study on interaction between macrocell and microcell in the early corrosion process of reinforcing s
A study on the initiation of pitting corrosion in carbon steel in chloride-containing media using sc
Study on the corrosion behavior of reinforcing steel in simulated concrete pore solutions using in s
The Electrochemical Characteristics of Pitting for Two Steels in Phosphate Buffer Solution with Chlo
Corrosion behavior of reinforcing steel in simulated concrete pore solutions: A scanning micro-refer
Corrosion initiation of stainless steel in HCl solution studied using electrochemical noise and in-s
A Phtoelectrochemical Study of Highly Ordered TiO2 Nanotube Arrays as the Photoanodes for Cathodic P
The degradation of passive film on carbon steel in concrete pore solution under compressive and tens
Effective monitoring of corrosion in reinforcing steel in concrete constructions by a multifunctiona
An in situ opticalQ1 second harmonic generation study of carbon steel in contact with an alkaline aq
Photocathodic protection properties of three-dimensional titanate nanowire network films prepared by
Probing the vertical profiles of potential in a thin layer of solution closed to electrode surface d
Sodium nitrite-based corrosion inhibitor for reinforcing steel in simulated polluted concrete pore s
Fabrication of heterostructured SrTiO3/TiO2 nanotube array films and their use in photocathodic prot
EIS analysis on chloride-induced corrosion behavior of reinforcement steel in simulated carbonated c
A study of the preparation and properties of the concrete for the bearing platform of the Xiamen-Zha
期刊信息
位置：