中文摘要：

通过静电纺丝法制备了聚醚砜（ PES ）/聚环氧乙烷-聚环氧丙烷-聚环氧乙烷三嵌段共聚物（ P123， PEO20PPO70PEO20，Ma=5800）纳米纤维膜，考察了P123含量对纺丝液的黏度和表面张力的影响，以及对所制备的纳米纤维膜的结构和性能的影响。实验结果表明：P123含量从3%（质量）增至9%时，其纺丝液的黏度由300 mPa·s增至1000 mPa·s，表面张力在36.5～37.8 mN·m-1范围内；P123改性的PES纳米纤维直径约为360 nm，分布均匀，其表面也比较光滑，取向趋于一致；此外，该纳米纤维膜具有良好的机械性能和耐溶胀性能，较大的比表面积（＞39 m2·g-1），孔隙率，可用作催化剂载体。

英文摘要：

Polyether sulfone （PES）/polyethylene oxide-polypropylene oxide-polyethylene oxide triblock copolymer （P123, PEO20PPO70PEO20,Ma=5800） nanofibrous membrane was preparedvia electrospinning. The influence of P123 content on viscosity and surface tension of spinning solution was investigated as well as the effect on structures and properties of the formed nanofibrous membranes. The results showed that the viscosity and surface tension of spinning solution increased from 300 to 1000 mPa·s and 36.5 to 37.8 mN·m-1 with increasing P123 content from 3% to 9%, respectively. The diameter of the obtained PES/P123 nanofibers was about 360 nm. The formed PES/P123 nanofibrous membranes had a uniform distribution, smooth surface and good mechanical and swelling properties. They also had large specific surface area （〉39 m2·g-1） and porosity, and could be used as catalyst support.