中文摘要：

采用溶剂热和溶液法合成了锂离子电池负极材料2，6．萘二酸锂（Li2NDC）三维配位聚合物。通过傅立叶红外光谱（FT．IR）、XRD和SEM等方法对样品进行分析；以50mA／g的电流在0．2—3．0V充放电，测试电化学性能。1molLi2NDC在首次放电时可嵌入2mol Li＋，放电平台位于0．75V处。溶剂热法、溶液法合成的Li2NDC，平均粒径分别为50弘m和3Ixm，第50次循环的放电比容量分别为60．8mAh／g和156．9mAh／g。

英文摘要：

A 3 D 2,6-napthalenedicarboxylate lithium（ Li2 NDC）coordination polymer as anode material for Li-ion battery was syn- thesized by solvothermal and solution method. Samples were analysized by Fourier transform infrared spectrometer（ FT-IR）, XRD and SEM methods. Electrochemical performance was tested by charged-discharged in 0.2 ~ 3.0 V with current of 50 mA/g. 1 mol Li2 NDC eould insert 2 mol Li ~ in initial discharge with a discharge plateau located near 0.75 V. The average particle sizes of Li2 NDC synthesized by solvothermal method and solution method were 50 Ixm and 3μm, respectively, the discharge specific capaci- ties at the 50th cycle were 60. 8 mAh/g and 156.9 mAh/g,respectively.