中文摘要：
采用铸锭冶金法制备了含稀土La和Zr的Al-Mg-Ti合金,通过力学性能测试及金相显微镜、扫描电镜、能谱和X射线衍射仪,观察分析了La、Zr微合金化对Al-Mg-Ti合金微观组织和力学性能的影响。结果表明,添加0.2%Zr能有效细化Al-Mg-Ti合金晶粒,说明Ti、Zr的细化作用是相容的,同时基体中析出的脆硬相Al_3Zr能显著提高合金硬度,但弱化了晶粒细化对合金强度和塑性的影响。0.2%La和0.2%Zr复合添加时的细化效果更为显著,合金的平均晶粒尺寸仅为55μm,同时La的添加有效避免了脆硬相Al_3Zr的析出和粗化,使合金的强度和塑性都得到了显著的提高,而硬度变化较小。
英文摘要：
Al-Mg-Ti alloys containing La and Zr elements were prepared by cast metallurgy.Effects of La and Zr additions on microstructure and mechanical properties of Al-Mg-Ti alloy were investigated by mechanical property test,optical microscopy,scanning electron microscopy,energy spectrum and X-ray diffraction.The results show that the addition of 0.2%Zr can positively refine the grain size,which indicates the composite refining effect of Ti and Zr is compatible,and the brittle phases of Al_3Zr precipitated in matrix can significantly increase the hardness of the alloys,but weaken the effect of grain refinement on the strength and ductility of the alloy.The combined addition of 0.2%La and 0.2%Zr possesses the excellent grain refining effect,when the average grain size of the alloy drops to only about 55 μm and the addition of La effectively avoids the precipitation and coarsening of brittle phase of Al_3Zr,thus improving the strength and ductility with the hardness changing slightly.
同期刊论文项目
同项目期刊论文
Effect of Inoculants Ti and Zr on Microstructure and Mechanical Properties of 2519 Al-Cu Alloy Welds
Effect on LY12 aluminum alloy welding joint microstructure and properties with Electron Beam Welding
Effect of compound inoculants Ti and Zr on as cast microstructure and mechanical properties of Al-Cu
Study on the microstructure and properties of resistance spot welding joint for ultra fine-grained s
Effect of rotary direction and speed on mechanical properties in friction stir spot welding of A6061
Microstructure and mechanical property of multi-walled carbon nanotubes reinforced aluminum matrix c
Effect of plunge speeds on hook geometries and mechanical properties in friction stir spot welding o
Microstructure and Mechanical Properties of Aer Met 100 Ultra-high Strength Steel Joints by Laser We
期刊信息
位置：