采用液相烧结工艺制备90W-Ni-Mn合金,研究锰含量对合金相对密度和抗拉强度的影响,并通过扫描电镜（SEM）观察试样断口形貌,利用金相显微镜观察样品显微组织。结果表明,随着锰含量增加,合金的相对密度和抗拉强度均降低,在1280℃保温2h得到的90W-8Ni-2Mn合金相对密度达97.32%,抗拉强度为702.50MPa;合金的整体密度和抗拉强度较低,主要是由于锰的化学活性很高,烧结过程中在相界面上易生成Mn的氧化物中间相,导致合金的孔隙度较大,从而降低合金的密度和抗拉强度。
英文摘要：
The effect of Mn content on relative density and tensile strength of 90W-Ni-Mn alloy prepared by liquid phase sintering has been studied. Fracture morphology and microscopic structure are investigated by SEM and metallographic microscope, respectively. The relative density and tensile strength of 90W-Ni-Mn have also been explored. The results show the relative density and tensile strength decrease with increasing Mn content. The relative density of 90W-8Ni-2Mn alloy sintered at 1 280 ℃ for 2 h is 97.32% and the tensile strength is 702.50 MPa. Middle phase of Mn oxide forms at phases interface, resulting in the porosity increase and relative density/tensile strength decrease.
同期刊论文项目
同项目期刊论文
Effect of strain rate on the compressive behaviour of a Zr56Al10.9Ni4.6Cu27.8Nb0.7 bulk metallic gla
Conversion of natural egg-shell to 3D flower-like hydroxyapatite agglomerates for highly sensitive d
Sea cucumber-like hydroxyapatite: cation exchange membrane-assisted synthesis and its application in
In situ formation of La containing dispersed phase on the sinter skin of La2O3 and Cr3C2 unitedly do
Influence of copper content on the microstructure and hardness of copperdoped tungsten carbide-cobal
期刊信息
位置：