中文摘要：

The heated test pieces were treated with alternating magnetic field by self-made experimental facility firstly. And influences of magnetic treatment on microstructure densification of Diamond Saw Segments were studied through hardness testing, ultrasonic testing, metallurgical structure and fracture pattern analysis by comparative method. The mechanism of magnetic treatment is analyzed and discussed in the end. The results show that the hardness of test pieces after magnetized are harder than before, that HRB hardness is improved by 3.58 on average. The sound path and amplitude of echo wave both decrease in test pieces after magnetized. The relative pad value of echo wave is regularly related with the microstructure densification, what is profound to further establish the regularity studying the degree of matrices densification using ultrasonic testing. The pores become few and pore shape gradually spheroidizing with the magnetic treatment, and matrices are more homogeneous and compact than the without by metallographic microscope. The degree of matrices densification is further improved after magnetized. The average crystal grain size is finer than the without, and the reason of grain refining is that densification of diamond saw blade improved. Magnetic treatment can act as one kind of effective technique to improve the microstructure densification of diamond saw segments.

英文摘要：

The heated test pieces were treated with alternating magnetic field by self-made experimental facility firstly. And influences of magnetic treatment on microstructure densification of Diamond Saw Segments were studied through hardness testing, ultrasonic testing, metallurgical structure and fracture pattern analysis by comparative method. The mechanism of magnetic treatment is analyzed and discussed in the end. The results show that the hardness of test pieces after magnetized are harder than before, that HRB hardness is improved by 3.58 on average. The sound path and amplitude of echo wave both decrease in test pieces after magnetized. The relative pad value of echo wave is regularly related with the microstructure densification, what is profound to further establish the regularity studying the degree of matrices densification using ultrasonic testing. The pores become few and pore shape gradually spheroidizing with the magnetic treatment, and matrices are more homogeneous and compact than the without by metallographic microscope. The degree of matrices densification is further improved after magnetized. The average crystal grain size is finer than the without, and the reason of grain refining is that densification of diamond saw blade improved. Magnetic treatment can act as one kind of effective technique to improve the microstructure densification of diamond saw segments.