中文摘要：
研究LZ50车轴钢不同过盈配合接触应力水平对旋转弯盐微动疲劳寿命的影响.分别利用光学显微镜、扫描电子显微镜对过盈配合表面的微动损伤表面和断口进行分析.结果表明,随着过盈量的增加,LZ50车轴钢旋转弯曲微动疲劳寿命呈现先降低而后升高的非线性特征,这是多轴复杂应力、配合面的接触应力、微动摩擦应力以及微动磨损交互作用的结果.
英文摘要：
LZ50 railway axle steel were carried out to study the effects of contact stress on rotating bending fretting fatigue life under different press-fit contact stresses. Optical microscope （OM） and Scanning electron microscope （SEM） were used to analyze the press-fit fretting damage surfaces and fracture surfaces, respectively. The results show that the rotating bending fretting fatigue life of the LZ50 present a nonliner feature, decrease with the increase of contact stress firstly, and then increase. It is due to the combination of the complex multiaxial stress of sample, contact stress between contact interfaces, fretting frication stress and the interaction between fretting wear and fretting fatigue.
同期刊论文项目
同项目期刊论文
Real time observation and friction vibration analysis of torsional fretting wear of polymethylmethac
An experimental study on bending fretting fatigue characteristics of 316L austenitic stainless steel
Torsional wear behaviors of UHMWPE against Ti6Al4V alloy and alumina femoral head ball in dry condit
Comparison on the torsional fretting wear of nitrogen ion implanted pure titanium and Ti6Al7Nb alloy
The Torsional Fretting Wear Behavior of Nitrogen Ion Implantation Layer of Ti6Al7Nb Ally Under Bovin
期刊信息
位置：