中文摘要：
以商品活性炭YP-15为电极材料,采用普通搅拌混浆和辅助超声搅拌混浆制备活性炭电极,研究了混浆方式对活性炭电极电容性能的影响。结果表明：与普通搅拌混浆相比,超声波混浆能够提高导电剂在活性炭中的分散性和均匀性,所制活性炭电极具有更佳的综合电化学性能。超声混浆所制备活性炭电极的放电比电容达到98.6 F/g,高于普通混浆活性炭电极的92.2 F/g;由于超声混浆活性炭电极的内阻更小,具有优异的比能量与功率特性,能够实现23.03Wh/kg的最大比能量和大于5 000 W/kg的最大比功率;且具有非常优异的循环性能,经过5 000次循环放电比电容衰减率仅为2.3%。因此,超声辅助混浆是制备高性能超级电容器活性炭电极的一种较为理想的前处理方法。
英文摘要：
In order to investigate the effect of slurry mixing mode on the capacitance performance of activated carbon（AC） electrode,YP-17 was treated by stirring and ultrasonic agitation to prepare the AC electrode,respectively.It is suggested that ultrasonic can dramatically improve the dispersion and uniformity of conductive agent in activated carbon which contributes to the better electrochemical performance,in comparison with normal stirring.The AC electrode prepared by ultrasonic shows a discharge specific capacity of 98.6 F/g,which is higher than that of 92.2 F/g by stirring method.Due to the lower residence of AC electrode made by ultrasonic method,it shows an excellent energy density of 23.03 Wh/kg and a power density above 5 000 W/kg.Moreover,it presents excellent long cycle life with high discharge capacity retention of 97.7% after 5 000 cycle.Therefore,ultrasonic is a promising pre-treatment mode for preparing high performance super capacitor with AC as electrode materials.
同期刊论文项目
同项目期刊论文
Hierarchical porous carbonmicrospheres derived from porous starch for use in high-rate electrochemic
One step productionof in-situ nitrogen doped mesoporous carbon confined sulfur for lithium-sulfurbat
Composite ofmesocarbon microbeads/hard carbon as anode material for lithium ion capacitorwith high e
Properties and Sodiuminsertion behavior of Phenolic Resin-based hard carbon microspheres obtained by
A novel electrolyteused in high working voltage application for electrical double-layer capacitorusi
Different types ofpre-lithiated hard carbon as negative electrode material for lithium-ioncapacitors
Electrochemical Performance of Electrospun carbon nanofibers as free-standing and binder-free anodes
Mesoporous carbon with large pore volume and high surface area prepared by a co-assembling route for
C/LiFePO4/multi-walled carbon nanotube cathode material with enhanced electrochemical performance fo
Effect of pre-lithiation degrees of mesocarbon microbeads anode on the electrochemical performance o
Nanostructured SiO2/C composites preparedvia electrospinning and their electrochemical properties fo
Lignin-basedelectrospun carbon nanofibrous webs as free-standing and binder-free electrodesfor sodiu
Effect ofreduction heat treatment in H2 atmosphere on structure ectrochemical properties of activate
Effect of the capacity design of activated carbon cathode on theelectrochemical performance oflithiu
A new route forsynthesizing C/LiFePO4/multi-walled carbon nanotube secondary particlesfor lithium io
An electrospunlignin/polyacrylonitrile nonwoven composite separator with high porosity and thermalst
Pre-lithiation designand lithium ion intercalation plateau utilization of mesocarbon microbeadsanode
Excellent lowtemperature performance electrolyte of spiro-(1,1′)-bipyrrolidiniumtetrafluoroborate by
Spiro-(1, 1′)-bipyrrolidinium tetrafluoroborate salt as high voltage electrolyte for Electric double
Hierarchical porous carbon microspheres derived from porous starch for use in high-rate electrochemi
ElectrospunPitch/Polyacrylonitrile composite carbon nanofibers as high performance anodesfor lithium
C/LiFePO4/multi-walledcarbon nanotube cathode material with enhanced electrochemical performance for
Facile synthesis of mesophase pitch/exfoliated graphite nanoplatelets nanocomposite and its applicat
Electrochemical Performance of Lithium Ion Capacitors Using Li+-Intercalated Mesocarbon Microbeads a
期刊信息
位置：