中文摘要：

为降低合成钛酸铝材料的原料成本，以铁合金厂铝钛渣为主要原料，按71．5％（加）铝钛渣和28．5％（ω）二氧化钛粉的基础配方，分别外加质量分数1％、2％、3％和4％的添加剂镁铝尖晶石，以聚乙烯醇溶液为结合剂，经湿磨、干燥、机压成型后，分别在1400、1450和1500℃保温2h合成了钛酸铝材料，然后检测其体积密度和显气孔率，运用XRD和SEM分析物相组成和显微结构，并运用X’Pert Plus软件计算钛酸铝的晶格常数。结果表明：镁铝尖晶石中Mg^2＋对钛酸铝中Ti^4＋的置换作用导致钛酸铝的晶格常数增大，晶格发生畸变，从而促进钛酸铝的合成及其烧结；随着合成温度的升高，上述置换作用和促进钛酸铝合成、烧结的效应增强。

英文摘要：

Aluminum titanate material was prepared using alumina titania slag from ferroalloy factory as the main raw material, basing on the basic formulation of 71.5% （in mass,the same hereinafter） alumina ti- tania slag and 28.5% titanium dioxide powder,extra adding 1% ,2% ,3% and 4% of magnesium aluminate spinel as additive, respectively, adding polyvinyl alcohol solution as binder, wet milling, drying, pressing, then firing at 1 400, 1 450 and 1 500℃ for 2 h in order to cut raw materials cost of synthesizing aluminum titanate material. The BD and AP of the synthesized material were determined,the phase composition and microstructure were analyzed using XRD and SEM,and the aluminum titanate lattice constants of the syn- thesized material were determined using X＇ Pert Plus software. The results show that the Mg^2＋ in spinel re- places Ti^4＋ in aluminum titanate,causing the increase of aluminum titanate lattice constants and the distor- tion of crystal lattice, thus accelerating the synthesis and sintering of aluminum titanate; with the temperature rising ,the replacing and accelerating-effects strengthen.