Fatigue and fracture behavior of nickel-based superalloy Inconel 718 up to the very high cycle regime
  • ISSN号：1673-565X
  • 期刊名称：《浙江大学学报：A卷英文版》
  • 时间：0
  • 分类：TG142.24[金属学及工艺—金属材料;一般工业技术—材料科学与工程;金属学及工艺—金属学] TG146.15[金属学及工艺—金属材料;一般工业技术—材料科学与工程;金属学及工艺—金属学]
  • 作者机构：[1]Applied Mechanics Laboratory, Department of Engineering Mechanics, School of Aerospace, Tsinghua University, Beijing 100084, China, [2]Mitsubishi Heavy Industries, Ltd., Tokyo, Japan
  • 相关基金：Project supported by the National Natural Science Foundation of China （Nos. 10872105 and 51071094）, and the Mitsubishi Heavy Industries, Ltd., Japan.Acknowledgements The authors gratefully thank the Mitsubishi Heavy Industries, Ltd., Japan for financial supports, and Dr. Xie in the Institute of Mechanics, Chinese Academy of Sciences for help in setting up the fatigue tests.
作者： Xian-feng MA, Zheng DUAN, Hui-ji SHI, Ryosuke MURAI, Eiichi YANAGISAWA
关键词： 疲劳裂纹萌生, Inconel, 镍基合金, 断裂行为, 循环, 疲劳裂纹扩展, 寿命预测模型, 温度试验, Nickel-based superalloy, High cycle fatigue （HCF）, Fatigue crack initiation, Crack growth, Life prediction
中文摘要：

Corresponding author E-mail： maxianfeng@gmail.com; Corresponding author E-mail： shihj@mail.tsinghua.edu.cn

同期刊论文项目
大型燃气轮机叶片镍基单晶材料的高温疲劳-蠕变性能研究
期刊论文 13
表面再结晶层对镍基高温合金疲劳性能影响的研究
期刊论文 11 会议论文 5
同项目期刊论文
Effect of heat treatment at 900 C in microstructural and mechanical properties of thermal barrier co
高温结构材料的蠕变和疲劳研究的一些新进展
Fatigue and fracture behavior of nickel-based superalloy Inconel 718 up to very high cycle regime
Influence of welding technique and temperature on fatigue properties of steel deposited with Co-base
In-situ scanning electron microscopy studies of small fatigue crack growth in recrystallized layer o
Gigacycle fatigue behaviors of two SNCM439 steels with different tensile strengthes
热障涂层-基体体系界面高温疲劳和断裂性能的实验研究
Failure characteristics and life prediction for thermally cycled thermal barrier coatings
In-situ scanning electron microscopy studies of small fatigue crack growth in ultrasonic consolidati
高温结构材料的蠕变和疲劳研究的一些新进展
On the fatigue small crack behaviors of directionally solidified superalloy DZ4 by in situ SEM obser
Fish-eye shape prediction with gigacycle fatigue failure
Shock response of copper bicrystals with a Sigma 3 asymmetric tilt grain boundary
Gigacycle fatigue behaviors of two SNCM439 steels with different tensile strengths
Crystallographic analysis for fatigue small crack growth behaviors of a nickel-based single crystal
Determination of mixed-mode interfacial fracture toughness for thermal barrier coatings
In situ SEM studies of the low cycle fatigue behavior of DZ4 superalloy at elevated temperature: Eff
A 2-D mesoscopic model for the evaluation of creep damage induced by void growth in polycrystalline metals
热障涂层-基体体系界面高温疲劳和断裂性能的实验研究
期刊信息
  • 《浙江大学学报：A卷英文版》
  • 中国科技核心期刊
  • 主管单位:
  • 主办单位:浙江大学
  • 主编：
  • 地址：杭州浙大路38号，浙江大学学报《英文版》编辑部
  • 邮编：310027
  • 邮箱：jzus@zju.edu.cn
  • 电话：0571-87952276 87952331
  • 国际标准刊号：ISSN：1673-565X
  • 国内统一刊号：ISSN：33-1236/O4
  • 邮发代号:
  • 获奖情况:
  • 国内外数据库收录:
  • 被引量:215