中文摘要：
以间苯二酚-糠醛低聚物为炭前驱体,三嵌段共聚物F127为结构导向剂,通过悬浮辅助的蒸发诱导自组装乳化成球,高温炭化后得到有序中孔炭球.考察了乳化剂用量和搅拌速度对有序中孔炭球的粒径和表面形貌影响,嵌段共聚物F127与间苯二酚摩尔比（F127/R）及间苯二酚-糠醛反应时间对有序中孔炭球的微观结构影响.结果表明：当乳化剂用量从0.1vol%增加到2.0vol%,有序中孔炭球的粒径从400μm减小到100μm;在乳化剂用量相同时,搅拌速度从100r/min增加到600r/min,有序中孔炭球的粒径从341μm减小到60μm;当F127/R的比值为0.008、0.015和0.025时,分别制得三维体心立方、二维六方和无序蠕虫结构的中孔炭球.
英文摘要：
Ordered mesoporous carbon spheres （OMCs） were synthesized by suspension-assist evaporationinduced self-assembly of resorcinol-furfural oligomers and triblock copolymer F127. The effects of emulsifier concentration and stirring speed on the particle size and morphology of OMCs were investigated. The effects of F127/resoncinol ratio and reaction time of resorcinol with furfural on the mesostructure of OMCs were evaluated. It is found that the paticle size can be controlled in the range from 60μm to 400μm by changing emulsifier concentration from 0. lvol% to 2.0vol% or stirring speed from 100r/min to 600r/min. The meso- structure of OMCs can be turned by varying the F127/resoncinol ratio or the reaction time of resorcinol with furfural. OMCs with 3-D body-centered cubic, 2-D hexagonal and wormlike mesostruetures are obtained with the F127/resoncinol ratio of 0. 008, 0. 015 and 0. 025, respectively.
同期刊论文项目
同项目期刊论文
The superior electrochemical performance of oxygen-rich activated carbons prepared from bituminous c
Molecular design of polymer precursors for controlling microstructure of organic and carbon aerogels
Effect of template and precursor chemistry on pore architectures of triblock copolymer-templated mes
Modification of polystyrene-based activated carbon spheres to improve adsorption of dibenzothiophene
Influence of nitrogen hetero-substitution on the electrochemical performance of coal-based activated
Fabrication of hierarchical porous carbide-derived carbons by chlorination of mesoporous titanium ca
Asymmetric capacitance response from the chemical characteristics of activated carbons in KOH electr
Capacitive matching of pore size and ion size in the negative and positive electrodes for supercapac
New concept of in situ carbide-derived carbon/xerogel nanocomposite materials for electrochemical ca
Facile synthesis of hierarchically structured Fe(3)O(4)/carbon micro-flowers and their application t
Ion Transport Behavior in Triblock Copolymer-Templated Ordered Mesoporous Carbons with Different Por
Genetic algorithm-least squares support vector regression based predicting and optimizing model on c
Preparation of Highly- Conductive CNTs/Polyaniline Composites through Plasma Pretreating and In-situ
Hollow carbon nanospheres prepared by carbonizing polymethylmethacrylate/polyacrylonitrile core/shel
Surface modification of pitch-based spherical activated carbon by CVD of NH3 to improve its adsorpti
Preparation and microstructure control of carbon aerogels produced using m-cresol mediated sol-gel p
期刊信息
位置：