中文摘要：
静电纺取向纳米纤维具有各向异性的微观结构与较高的力学性能,因此具有更广泛的应用。利用一种新型的静电纺收集装置制备取向聚乳酸（PLLA）纳米纤维,该收集装置包括一个旋转的滚筒和两块平行电极。为进一步研究该收集装置制备取向纳米纤维的机理,利用Ansoft Maxwell电磁模拟软件模拟了静电纺过程中的电场分布。制得的取向PLLA纳米纤维的直径为（405±102）nm,扫描电子显微镜（SEM）显示,该PLLA纳米纤维具有较好的取向性,取向排列程度为91.2%。力学拉伸试验显示,取向PLLA纳米纤维的力学性能具有各向异性,其拉伸强度、断裂伸长率和杨氏模量都远大于普通非取向PLLA纳米纤维。
英文摘要：
Aligned electrospun nanofibers,which possessed anisotropic microstructure and better mechanical properties,had more promising application. A novel electrospinning collector,consisting of a rotating drum and 2 parallel electrodes,was used to prepare aligned nanofibers. To further validate the fabrication of aligned nanofibers,the electric field distribution of electrospinning was simulated by the electromagnetic simulation software,Ansoft Maxwell. Well-aligned poly（ L-lactic acid）（ PLLA） with the diameter of（ 405 ± 102） nm nanofibers was manufactured and scanning electron microscopy（ SEM） images showed that the aligned PLLA nanofibers had directional morphology with aligned degree of 91. 2%. The tensile test expressed that aligned PLLA nanofibers possessed anisotropic mechanical properties,and their tensile strength,tensile strain and Young＇s modulus were remarkably higher than random PLLA nanofibers.
同期刊论文项目
同项目期刊论文
Biocompatibility evaluation of protein-incorporated electrospun polyurethane-based scaffolds with sm
Dual functions of polyvinyl alcohol(PVA):fabricating particles and electrospinning nanofibers applie
Poly-3-hydroxybutyrate-co-3-hydroxyvalerate containing scaffolds and their integration with osteobla
An improved free surface electrospinning with micro-bubble solution system for massive production of
Polyacrylonitrile nanofiber yarns and fabrics produced using a novel electrospinning method combined
Guiding the orientation of smooth muscle cells on random and aligned polyurethane/collagen nanofiber
Biocomposite scaffolds for bone regeneration:Role of chitosan and hydroxyapatite within poly-3-hydro
The structure and properties of cellulose acetate materials: A comparative study on electrospun memb
Dual functions of polyvinyl alcohol (PVA): fabricating particles and electrospinning nanofibers appl
From macro to micro to nano: the development of a novel lysine based hydrogel platform and enzyme tr
A reversible colorimetric chemosensor for naked-eye detection of copper ions using poly (aspartic ac
Uniaxially aligned polyacrylonitrile nanofiber yarns prepared by a novel modified electrospinning me
期刊信息
位置：