The coverage and temperature-dependent nucleation behaviors of the Gd@C82 metallofullerenes on Cu(111) have been studied by low-temperature scanning tunneling microscopy (LT-STM) in detail. Upon molecular deposition at low temperature, Gd@C82 molecules preferentially decorate the steps and nucleate into single layer islands with increasing coverage. Further annealing treatment leads some of the Gd@C82 molecules to assemble into bright and dim patches, which are correlated to the adsorption induced substrate reconstruction. Upon sufficient thermal activation, Gd@C82 molecules sink into the Cu(111) surface one-copper-layer-deep, forming hexagonal close-packed molecular islands with intra-molecular details observed as striped patterns. By considering the commensurability between the Gd@C82 nearest-neighbor distance and the lattice of the underlying Cu(111), we clearly identified two kinds of in-plane molecular arrangements as (19(1/2)×19(1/2))R23.4°and (19(1/2)×19(1/2))R36.6°with respect to Cu(111). Within the assembled Gd@C82 molecular, island molecules with dim-bright contrast are spatially distributed, which may be modulated by the preexisted species on Cu(111).

英文摘要：

The coverage and temperature-dependent nucleation behaviors of the Gd@C82 metallofullerenes on Cu（111） have been studied by low-temperature scanning tunneling microscopy （LT-STM） in detail. Upon molecular deposition at low temperature, Gd@C82 molecules preferentially decorate the steps and nucleate into single layer islands with increasing coverage. Further annealing treatment leads some of the Gd@C82 molecules to assemble into bright and dim patches, which are correlated to the adsorption induced substrate reconstruction. Upon sufficient thermal activation, Gd@C82 molecules sink into the Cu（111） surface one-copper-layer-deep, forming hexagonal close-packed molecular islands with intra-molecular details observed as striped patterns. By considering the commensurability between the Gd@C82 nearest-neighbor distance and the lattice of the underlying Cu（111）, we clearly identified two kinds of in-plane molecular arrangements as （19（1/2）×19（1/2））R23.4°and （19（1/2）×19（1/2））R36.6°with respect to Cu（111）. Within the assembled Gd@C82 molecular, island molecules with dim–bright contrast are spatially distributed, which may be modulated by the preexisted species on Cu（111）.