中文摘要：

采用固相反应法，制备了Ba3（Co0.4Zn0．6）2Fe24O4Z型六方铁氧体。研究了Bi2O3-MgO复合掺杂对低温烧结Ba3（Co0．4ZnO6）2Fe24O4Z型六方铁氧体的显微结构和电磁性能的影响。结果表明：在固定w（Bi2O3）为3．0％的基础上，当掺入的w（MgO）为0．6％时，此Z型六方铁氧体可在900℃下低温烧结，高频电磁性能得到了显著的提高，材料在300MHz时的磁品质因数Q值从7．1提高到14．5，εr和tanδ分别从16．0和0．04100降低到10．8和0．00355，有望成为高频片式电感用材料。

英文摘要：

Ba3（Co0.4Zn0.6）2Fe24O4 Z-type hexaferrites were prepared by a solid-state reaction method. Effects of Bi2O3-MgO co-doping on the microstructure and electromagnetic properties of low temperature sinted Ba3（Co0.4Zn0.6）2Fe24O4 Z-type hexaferrite materials were investigated. It is found that the high-frequency electromagnetic properties of Ba3（Co0.4Zn0.6）2Fe24O4 Z-type hexaferrite materials are increased remarkably by Bi2Oa-MgO co-doping, on the basis of Bi2O3 doping in a fixed amount of 3.0% （mass fraction）, with the addition of MgO reaches 0.6% （mass fraction）, the magnetic quality factor Q value increases from 7.1 to 14.5, the εr and tanδ decrease from 16.0 and 0.041 00 to 10.8 and 0.003 55 at 300 MHz. Electromagnetic properties of the Z-type hexaferrites satisfy the requirements of producing MLCI.