采用包埋法在C／C复合材料表面制备了SiC高温防氧化涂层。利用SEM和XRD等方法对涂层的微观形貌和晶相组成进行了观察与分析，并对带涂层试样在室温-1500℃范围内的氧化行为进行了研究。结果表明，涂层主要由β—SiC和少量的游离si组成，涂层表面有裂纹存在，涂层与C／C复合材料基体结合良好，呈现犬牙状结合。在室温-1500℃之间，带SiC涂层C／C复合材料的氧化行为可分为4个阶段，涂层在高温区具有较好的防氧化性能。
英文摘要：
An anti-oxidation SiC coating prepared with pack cementation process was applied to protect C/C composites from oxidation at high temperature. The microstructure and composition of SiC coating was analyzed with SEM and XRD. The oxidation behavior of the composites with SiC coating from room temperature to 1 500 ℃ was investigated. The results show that the as-re- ceived coating is mainly composed of β-SiC with a little of Si and there exist a few microcracks on the coating surface. Further ob- servation reveals that the SiC coating is perfectly packed on the C/C composites with interlocked bonding. The oxidation behavior of the coated C/C composites can be divided into four parts from room temperature to 1 500 ℃, and the coating shows excellent oxida- tion resistances at high temperature
同期刊论文项目
同项目期刊论文
Microstructures and Ablation Resistance of ZrC Coating for SiC-Coated Carbon/Carbon Composites Prepa
Anti-oxidation property of a multi-layer coating for carbon/carbon composites in a wind tunnel at 15
MoSi2-based oxidation protective coatings for SiC-coated carbon/carbon composites prepared by supers
A MoSi2-SiC-Si/MoSi2 coating to protect carbon/carbon composites against oxidation at 1700 degrees C
Oxidaiton resistant (Mo,W)Si2 coating for SiC-coated carbon/carbon composites by in situ formation m
Fabrication of Isotropic Pyrocarbon at 1400℃ by Thermal Gradient Chemical Vapor Deposition Apparatus
Carbon nanotube-templated copper phthalocyanine derivative assemblies via solid-phase synthesis: eff
Microstructure and anti-oxidation properties of multi-composition ceramic coatings for carbon/carbon
A Si-SiC oxidation protective coating for carbon/carbon composites prepared by a two-step pack cemen
Oxidation protection of carbon/carbon composites with SiC/indialite coating for intermediate tempera
Finite element simulation of the effects of process parameters on deposition uniformity of chemical-
Effect of thermal shock and oxidation on mechanical property of carbon/carbon composites with a sili
Finite element simulation of effects of process parameters on deposition rate of SiC by chemical vap
Oxidation protective C/SiC/Si-SiC multilayer coating for carbon/carbon composites applying at 1873 K
期刊信息
位置：