采用水溶性低分子质量酚醛树脂处理杉木试样,使用纳米压痕测试技术对其管胞细胞壁的弹性模量和硬度进行测试。结果表明：处理试样管胞细胞壁的平均弹性模量和硬度比对照试样分别增加了32.94%和32.93%。使用紫外显微分光光度计分析得知,处理试样管胞细胞壁的吸光度远高于对照试样,说明低分子质量的酚醛树脂能够扩散进入到纳米级孔隙的杉木管胞细胞壁S2层内,并最终引起细胞壁力学性质的增加。
英文摘要：
The mechanical properties of wood-based materials can be improved significantly by the modification of low molecular weight phenol-formaldehyde resin.In this paper,the samples of Chinese fir were treated by low molecular weight phenol-formaldehyde resin,then the cell wall mechanical properties of tracheids of PF treatment and untreated reference samples were tested by the technique of nanoindentation.Compared with untreated reference samples,the increases in the average modules of elasticity of 32.94% and in the average hardness of 32.93% were observed for PF treatment samples.The absorbance of PF treatment samples was higher than the untreated reference samples by the analysis of ultraviolet micro-spectrophotometer.This proves clearly that the low molecular weight phenol-formaldehyde resin was able to diffuse into the nanopores in the S2 layer of tracheids cell wall of Chinese fir.Thus,the mechanical properties of cell wall could be improved.
同期刊论文项目
同项目期刊论文
Use of Visible and Near Infrared Spectroscopy to Predict Klason Lignin Content of Bamboo, Chinese Fi
Rapid Estimation of Microfibril Angle of Increment Cores of Chinese Fir by Near Infrared Spectroscop
Anatomical characteristics, chemical and mechanical properties of fast-grown plantation Populus X eu
Effect of plant age on the mechanical properties of moso
bamboo (phyllostachys heterocycla var. pube
Surface deterioration of moso bamboo (Phyllostachys pubescens) induced by exposure to artificial sun
Longitudinal mechanical properties of cell wall of Masson pine (Pinus massoniana Lamb) as related to
Distinction of Three Wood Species by Fourier Transform Infrared Spectroscopy and Two-dimensional Cor
期刊信息
位置：