中文摘要：

采用区域熔炼法成功制备出了高质量、高纯度、大尺寸的LaB6、CeB6单晶体。系统分析了制备过程中每个参数对晶体生长的影响,确定了晶体成长最佳工艺：（1）LaB6：转速为30r/min,生长速度为8～10mm/h,两次区熔;（2）CeB6：转速为30r/min,生长速度15～20mm/h,一次区熔。然后对晶体进行表征,主要方法有单晶衍射、断面扫描、拉曼衍射、摇摆曲线。由此可知悬浮区域熔炼法是制备高质量、高纯度、大尺寸REB6的最佳方法。

英文摘要：

The high quality,high purity and large size LaB6,CeB6 single crystals had been successfully grown by optical floating zone method.Each parameter which impact in the process of crystal growth was studied in this article.We determine the optimum crystal growth：（1） LaB6： speed of 30r/min,the growth rate of 8-10mm/h,twice zone melting;（2） CeB6： speed of 30r/min,the growth rate of 15-20mm/h,once zone melting.And then analysis the characterizations of single crystals.We use the main method,and they are single crystal diffraction,Raman diffraction,rocking curve,cross-section scanning.These show that floating zone growth is the best method in the produced single crystal REB6（LaB6,CeB6） cathode.