中文摘要：
通过酸性浸出的方法从尾矿中分离出高纯度铁，并以此为原料采用还原一化学共沉淀法制备了Fe3O4纳米颗粒。经过TEM等手段的表征，结果表明颗粒平均粒径为10nm左右，且粒径分布均匀。实验研究了从尾矿中获得高纯度铁的工艺条件，并分析了工艺因素的影响机制。用振动样品磁强计室温下测量粉末样品的磁性能，磁滞回线表明所制备的样品具有超顺磁性。
英文摘要：
Iron is separated from tailings by acidic leaching method, and nanosized magnetic Fe3O4 powder is prepared using a reduction-coprecipitation method. TEM image shows that average particles size of the Fe3O4 is about 10nm and exhibit a uniformly distribution. The process conditions in which high-purity iron can be obtained is studied, and the affecting mechanism of these factors is analyzed. Magnetic properties of the sample are measured by vibrating sample magnetometer. The magnetic hysteresis loop shows that the sample has superparamagetism