用小角激光光散射（SALLS）、相差显微镜（PCM）、示差扫描量热仪（DSC）和偏光显微镜（POM）研究了聚丙烯／二元乙丙橡胶（iPP／EPR）共混体系的相分离行为和等温结晶行为，发现iPP／EPR（50／50，W／W）发生的液-液相分离遵循spinodal机理。通过Cahn—Hilliard方程求得了不同实验温度下iPP／EPR的表观扩散系数（Dapp）以及spinodal温度（Ts），考察了不同相分离程度的iPP／EPR体系结晶动力学，发现延长相分离时间（tps）或提高相分离温度（Tps）均会导致半结晶时间（t1/2）增大，即结晶速率降低。这被归于EPR成核作用的降低。动力学分析结果表明Avrami模型适用于描述该体系的等温结晶过程，其结晶机理基本不受相分离程度的影响，结晶均以瞬时成核和三维生长为主。
英文摘要：
The liquid-liquid phase-separation （LLPS） and isothermal crystallization behavior of isotactic polypropylene/ethylene-propylene rubber blend （iPP/EPR） were investigated by using small angle laser light scattering （ SALLS ）, differential scanning calorimetry （ DSC ）, phase contrast microscopy （ PCM ） and polarized optical microscopy （POM）. Results reveal that LLPS of （50/50, W/W） iPP/EPR blend happens at temperaturesabove the melting point of iPP,and its kinetics follows the spinodal decomposition （SD） mechanism. The apparent diffusion coefficient （Dapp） and the spinodal temperature （ Ts ） of the iPP/EPR samples were calculated on the basis of the Cabn-Hilliard theory. Moreover, it is found that the Dapp increases with the increase of temperature, representing the LCST behavior of iPP/EPR. The development of phase morphologies could be obtained byquenching in liquid N2 hand,the structure of i continuous phases form, the IPP/EPR samples subjected to annealing with different ti PP/EPR melt appears nearly homogenous at the beginning of and the phase connectivity grows until macroscopic spherical me at 200℃. On the Other LLPS. Furthermore, the cotexture generates. Both theincreases of phase separation time （tps） and phase separation temperature （Tps） result in the decrease of the crystallization rate. The kinetic results indicate that the Avrami model is qualified for describing the isothermal crystallization of iPP/EPR. It is believed that the degree of phase-separation has little effect on the crystallization kinetics and the crystallization gives priority to instantaneous nucleation and three-dimension-growth.
同期刊论文项目
同项目期刊论文
TIME AND TEMPERATURE DEPENDENCE OF PHASE-SEPARATION BEHAVIOR FOR POLY(N-METHYL METHACRYLIMIDE)/POLY(
Study on degradation and crosslinking of impact polypropylene copolymer by dynamic rheological measu
期刊信息
位置：