中文摘要：
以平均粒径为22μm和0．5μm的α-Al2O3粉体为起始原料（以下分别简称Al2O3（C）和Al2O3（F）），分别以聚乙烯亚胺（PEI）和聚甲基丙烯酸铵（APMA）为聚合物电解质，采用非均相凝固法将Al2O3（F）颗粒均匀地包覆在Al2O3（C）粉体表面．重点考察了聚合物电解质的吸附时间、Al2O3（C）／Al2O3（F）的质量比、两种分子量的PEI对包覆型氧化铝粉体制备的影响．当Al2O3（C）／Al2O3（F）的质量比为1：3，经过分子量约为60000的PEI处理2h的Al2O3（C）粉体表面均匀地包覆了Al2O3（F）颗粒（经APMA处理2h）．采用该包覆型粉体制备出片状多孔支撑体，其孔隙率为35．8％，平均孔径为2．9m，纯水通量为205m3／（m2·h·MPa）．
英文摘要：
Coated alumina powders were prepared by using α- Al2O3 with average particle size ot 22： μm and 0.5 μm as starting powders（hereafter mentioned as Al2O3 （C） and Al2O3 （F）, respectively） through heterocoag- ulation process was investigated.Al2O3 （F） particle was successfully coated on the surface of Al2O3 （C） by using ammonia polymethacrylate（APMA） and polyethylenimine（PEI） as polyelectrolyte dispersant, respectively. The effect of adsorption time of polyelectrolyte dispersant on the surface of alumina, the weight ratio of Al2O3（C）/ Al2O3（F） as well as the two PEI with different molecular weight on the result of coated powders was studied in detail. The optimal coating conditions was as follows： the weight ratio of Al2O3（C） to Al2O3（F） was 1：3, Al2O3（C） powder and Al2O3（F） powder was modified with PEI （MW = 60 000） and APMA for 2 h, respectively. Disk supports were prepared by using the coated alumina powders under the abovementioned optimal conditions and the property of such disk support was as follows, porosity： 35.8% ,average pore size： 2.9/μm, pure water flux： 205 m3/（m2·h·MPa）.
同期刊论文项目
同项目期刊论文
Preparation of Pd-B/TiO2 amorphous alloy catalysts and their performance on liquid-phase hydrogenati
The oxidative stream reforming of methane to syngas in a thin tubular mixed-conducting membrane reac
A new route for the fabrication of TiO2 ultrafiltration membranes with suspension derived from a wet
A novel route to synthesize nano-crystalline Ba0.5Sr0.5Co0.8Fe0.2O3?δ perovskite oxide at high tempe
Polydimethylsiloxane (PDMS)/ceramic composite membrane with high flux for pervaporation of ethanol-w
Chemical expansion, crystal structural stability, and oxygen permeability of SrCo0.4Fe0.6-xAlxO3?δ o
Organic–inorganic composite pervaporation membranes prepared by self-assembly of polyelectrolyte mul
Improving performance of a dense membrane reactor for thermal decomposition of CO2 via surface modif
Synthesis of nanocrystalline conducting composite oxides based on a non-ion selective combined compl
Match of thermal performances between the membrane and the support for supported dense mixed-conduct
A self-catalytic mixed-conducting membrane reactor for effective production of hydrogen from methane
Modeling of relationship between water permeability and microstructure parameters of ceramic membran
期刊信息
位置：