中文摘要：

应用水热-溶胶凝胶法合成了Li2MnSiO4正极材料.由XRD、FTIR、固体NMR及恒流充放电等方法表征、分析样品的相组成、晶体结构和电化学性能.结果表明,合成的样品主相为Li2MnSiO4,同时存在少量Li2CO3杂质.该材料的首次放电容量可达190mAh·g-1,但在充放电循环过程中由于结构坍塌、分解导致其容量衰退明显.

英文摘要：

The Li2MnSiO4 cathode material for lithium ion batteries was synthesized by sol-gel assisted hydrothermal method. XRD,FTIR and SS-NMR were used to study the phase,structure and morphology of obtained samples. Electrochemical performance of cathode material was tested. The results show that the main phase of sample prepared was Li2MnSiO4,whereas a small amount of impurities （ Li2CO3） were existed. The Li2MnSiO4 cathode material gave an initial discharging capacity of about 190 mAh·g -1. But this capacity faded rapidly during the cycling process due to the decomposition of Li2MnSiO4.