中文摘要：
合成了一种新型的有机／无机杂化钙钛矿（NH3C6H4OC6H4NH3）PbI4，采用元素分析、紫外一可见光吸收光谱、x射线衍射和透射电镜对其结构进行了表征，结果表明这种材料具有规则的层状结构，有序性高．对这种材料的薄膜进行了伏安测试，结果表明该材料属于n型半导体，其电子迁移率达到0．065cm^2·V^1·s^-1，在光电器件领域有着潜在的应用前景．
英文摘要：
A novel organic-inorganic hybrid material, （NH3C6H4OC6H4NH3）PbI4 with a perovskite struc- ture, was synthesized and characterized by elemental analysis, UV-Vis, X-ray diffraction （XRD） and TEM techniques. XRD patterns from its powder showed that the hybrid material was well-ordered and in layered frame. Electric measurements performed on the spin-coated films from the organic-inorganic hybrid material have demonstrated a room-temperature electron mobility as high as 0.065 cm^2·V^-1·s^- 1, which is a promising material for photoelectric devices.