中文摘要：
将SiC陶瓷粉末、醇-水混合溶剂、丙烯酰胺-亚甲基双丙烯酰胺凝胶体系以及堇青石-锂辉石复合烧结助剂配制成料浆,采用凝胶注模成型–烧结工艺制备SiC多孔陶瓷,研究烧结助剂用量和烧结温度对多孔SiC陶瓷的形貌与显微结构、物相组成以及强度、孔径、开孔率与渗透率等性能的影响。结果表明：温度高于1 300℃时,复合烧结助剂熔融形成固溶体,从而实现SiC多孔陶瓷的低温烧结;随烧结助剂用量增加或烧结温度升高,SiC多孔陶瓷的开孔率和气体渗透速率均下降。在料浆中SiC陶瓷粉体体积分数为20%、烧结助剂质量分数为10%、醇水体积比为7：3、锂辉石与堇青石质量比为2：1的条件下,于1 370℃烧结后得到的SiC多孔陶瓷,孔隙率高、孔径分布集中（4~15μm）,孔形貌呈均匀的三维无规则贯通结构,抗弯强度为8.5 MPa,开孔率达到67.9%,透气率为280.5 m~3/（m~2·Pa·h）。
英文摘要：
The SiC slurry was prepared using ethanol-water mixed solvent as the dispersion medium, acrylamide-methylene bis acrylamide as gel system and cordierite-spodumene as sintering additives. The porous SiC ceramics were fabricated by gelcasting-sintering process. The effects of sintering additive content and sintering temperature on the morphology, microstructure, phase composition, strength, pore size, open porosity and gas permeability of the sintered porous SiC ceramics were investigated. The results show that, when the temperature is higher than 1300 ℃, sintering additives absorb heat and form the low-temperature melting solid solution, which can effectively decrease sintering temperature of the SiC porous ceramic. With increasing the content of sintering additive and sintering temperature, both the porosity and gas permeability of the porous SiC ceramics decrease. At conditions of 20% volume fraction of SiC powder in the slurry, 10% mass fraction of sintering additive, 7：3 volume ratio of alcohol-water 2： I mass ratio of spodumene and cordierite and sintering temperature of 1370 ℃, the pores morphology of porous SiC ceramics are three dimensional irregular penetrating structure, and the porosity, flexural strength, pore size and gas permeability of SiC porous ceramics are 67.9%, 8.5 MPa, 4-15 pm and 280.5 rn3/（m2＂Pa-h）, respectively.
同期刊论文项目
同项目期刊论文
Osteoblastic cell response on biphasic fluorhydroxyapatite/strontium-substituted hydroxyapatite coat
Synthesis and optical property of ultra-long alpha-Si3N4 nanowires under superatmospheric pressure c
A thermodynamic description of the Co-Cr-Ti ternary system over the entire composition and temperatu
Development of an atomic mobility database for disordered and ordered fcc phases in multicomponent A
Thermodynamic description of the Al-Mg-Si system using a new formulation for the temperature depende
Experimental Investigation and Computer Simulation of Gradient Zone Formation in WC-Ti(C,N)-TaC-NbC-
Photosan-II loaded hollow silica nanoparticles: Preparation and its effect in killing for QBC939 cel
Effect of calcium on the electrochemical behavior of lithium anode in LiOH aqueous solution used for
Facile synthesis of Ag/AgVO3 hybrid nanorods with enhanced electrochemical performance as cathode ma
Thermodynamic description of the Ge-Na and Ge-K systems using the CALPHAD approach supported by firs
Investigation to impurity content and micromorphology of high purity titanium powder prepared by mol
Microstructures and mechanical properties of Fe-14Cr-3W-Ti-Y2O3 steel with 1 wt.% Cu addition fabric
Ideal mechanical strength and interface cohesion property of Ir-base superalloys from first principl
Effect of MWCNTs Additive on Desorption Properties of Zn(BH4)(2) Composite Prepared by Mechanical Al
Effects of Ca on microstructure, mechanical and corrosion properties and biocompatibility of Mg-Zn-C
Microstructural Evolution of a Nickel Ferrite-Copper Alloy Cermet During Sintering and High-Temperat
Innovative processing of high-strength and low-cost ferritic steels strengthened by Y-Ti-O nanoclust
Effect of tungsten content on microstructure and quasi-static tensile fracture characteristics of ra
Synthesis and characterization of superhydrophobic functionalized nanoparticle arrays on aluminum su
Preparation of Super-Hydrophobic Aluminum by a Novel Immersion Method using Potassium Permanganate S
Structural evolution and ablation mechanism of a hafnium carbide coating on a C/C composite in an ox
Experimental investigation and thermodynamic modeling of the Cu-Si-Zn system with the refined descri
THERMODYNAMIC MODELING OF THE Fe-Zn SYSTEM USING EXPONENTIAL TEMPERATURE DEPENDENCE FOR THE EXCESS G
Relationship between lamellar alpha evolution and flow behavior during isothermal deformation of Ti-
Effect of heat treatment on strength, exfoliation corrosion and electrochemical behavior of 7085 alu
First-principles calculations of binary Al compounds: Enthalpies of formation and elastic properties
Structure and thermodynamics of the key precipitated phases in the Al-Mg-Si alloys from first-princi
Development of an atomic mobility database for liquid phase in multicomponent Al alloys: focusing on
Fiber/matrix interfacial shear strength of C/C composites with PyC-TaC-PyC and PyC-SiC-TaC-PyC multi
Sol-hydrothermal synthesis and optical properties of Eu3+, Tb3+-codoped one-dimensional strontium ge
Flower-like hydroxyapatite modified carbon paste electrodes applicable for highly sensitive detectio
Comparison of microstructure and mechanical properties of Co-based and Fe-based alloy coatings depos
Thermodynamic assessment of the Ga-X (X=B, Ca, Sr, Ba) systems supported by first-principles calcula
Effect of heat treatment on hot deformation behavior and microstructure evolution of 7085 aluminum a
Ablation behavior of HfC protective coatings for carbon/carbon composites in an oxyacetylene combust
Effects of partial hydrogenation and vacancy defects on the electronic properties of metallic carbon
Effects of Cu and Al on the crystal structure and composition of eta (MgZn2) phase in over-aged Al-Z
Conversion of egg-shell to hydroxyapatite for highly sensitive detection of endocrine disruptor bisp
期刊信息
位置：