稀土元素的锡酸盐(行 ₂ Sn ₂ O ₇( 行 = Y， La-Lu )) 有 50 nm 的一条平均直径的 nanocrystals 通过灵巧的微波被准备在 200 点的热水的方法|

英文摘要：

Rare-earth stannate（Ln_2Sn_2O_7（Ln = Y, La–Lu）） nanocrystals with an average diameter of 50 nm were prepared through a facile microwave hydrothermal method at 200°C within 60 min. The products were well characterized. The effect of reaction parameters such as temperature, reaction time, p H value, and alkali source on the preparation was investigated. The results revealed that the p H value plays an important role in the formation process of gadolinium stannate（Gd_2Sn_2O_7） nanoparticles. By contrast, the alkali source had no effect on the phase composition or morphology of the final product. Uniform and sphere-like nanoparticles with an average size of approximately 50 nm were obtained at the p H value of 11.5. A possible formation mechanism was briefly proposed. Gd_2Sn_2O_7：Eu~（3＋） nanoparticles displayed strong orange-red emission. Magnetic measurements revealed that Gd_2Sn_2O_7 nanoparticles were paramagnetic. The other rare-earth stannate Ln_2Sn_2O_7（Ln = Y, La–Lu） nanocrystals were prepared by similar approaches.