中文摘要：
用微胶囊化得到的空心酚醛树脂微球制备出酚醛泡沫材料,在Ar气的保护下进行1000℃碳化和2000℃的石墨化处理,得到所需的泡沫材料.研究了孔隙率、热处理温度等因素对碳泡沫导热性能的影响.结果表明：提高材料内部空心微球的比例可以降低材料的导热性能,得到低热导率的泡沫材料;而对于孔隙率接近的泡沫材料,降低材料内部的孔径可以起到降低材料热导率的作用;得到了密度为0.50g/cm^3,热导率为1.007W/m·K,压缩强度为8.82MPa的碳泡沫材料.
英文摘要：
The phenolic resin foam was prepared by using hollow phenolic resin microspher which was made by microcapsule.And under the protection of At,the microcapsules were carbonized at 1000℃and graphited at 2000℃,then the foam was got.Herein the porosity and the effect of heat treatment temperature on carbon foam were investigated.And the results show that the porosity increasement can reduce the thermal conduction of material,and the low thermal conduction foam is obtained by using this method.However,for the materials with approximative porosity,the thermal conduction is decreased by reducing aperture of material.Finally,the foam material is obtained with density of 0.50g/cm3,thermal conduction of 1.007W/m·K and compressive strength of 8.82MPa.
同期刊论文项目
同项目期刊论文
Fabrication of Isotropic Pyrocarbon at 1400℃ by Thermal Gradient Chemical Vapor Deposition Apparatus
Carbon nanotube-templated copper phthalocyanine derivative assemblies via solid-phase synthesis: eff
Microstructure and anti-oxidation properties of multi-composition ceramic coatings for carbon/carbon
A Si-SiC oxidation protective coating for carbon/carbon composites prepared by a two-step pack cemen
Oxidation protection of carbon/carbon composites with SiC/indialite coating for intermediate tempera
Finite element simulation of the effects of process parameters on deposition uniformity of chemical-
Effect of thermal shock and oxidation on mechanical property of carbon/carbon composites with a sili
Finite element simulation of effects of process parameters on deposition rate of SiC by chemical vap
Oxidation protective C/SiC/Si-SiC multilayer coating for carbon/carbon composites applying at 1873 K
期刊信息
位置：