中文摘要：

采用等温热处理工艺制备具有半固态显微组织的Mg-8%Al-1%Si合金,研究等温热处理工艺参数（等温温度和等温时间）对Mg-8%Al-1%Si合金显微组织的影响。结果表明：通过等温热处理工艺可以得到具有非枝晶组织的Mg-8%Al-1%Si合金。随着等温温度从560°C升高至575°C或等温时间从5min延长至30min,半固态组织中的液相体积分数增加,α-Mg晶粒尺寸变大并且其球化趋势明显。此外,在半固态组织中的共晶Mg2Si相从汉字状转变成为颗粒状。研究等温热处理Mg-8%Al-1%Si合金中的共晶Mg2Si相的形貌转变机制。

英文摘要：

A Mg-8%Al-1%Si alloy with semisolid microstructure was fabricated by isothermal heat treatment process. The effects of isothermal process parameters such as holding temperature and holding time on the microstructure of Mg-8%Al-1%Si alloy were investigated. The results show that a non-dendritic microstructure could be obtained by isothermal heat treatment. With increasing holding temperature from 560 to 575 °C or holding time from 5 to 30 min, the liquid volume fraction increases, the average size of α-Mg grains grows larger and globular tendency becomes more obvious. In addition, the Mg2Si phase transforms from Chinese script shape to granule shape. The morphology modification mechanisium of Mg2Si phase in Mg-8%Al-1%Si alloy during the semisolid isothermal heat treatment was also studied.