中文摘要：
用溶胶-凝胶（Sol—gel）法制备La0.7Sr0.3MnO3（LSMO）靶材，用脉冲激光沉积（PLD）法在LaAlO3（O12）基片上沉积出厚度约为187nm的LSMO薄膜，研究了真空退火对薄膜的输运和光诱导特性的影响．结果表明，薄膜的相变温度随着退火时间的增加而降低，薄膜的电阻率升高．在低温金属相光照使电阻率降低，在高温绝缘相光照则使电阻率升高．随着退火时间的增加，光电导（△p）先增大而后减小，在真空条件下退火40min的薄膜光电导（△p）达到最大值为0．013Ωcm．根据双交换作用解释了薄膜光电导的变化规律．
英文摘要：
La0.7Sr0.3MnO3 （LSMO） target has been prepared by a Sol-gel method and the film of LSMO with the thickness of 187 nm has been deposited on a （012）-oriented LaAlO3 substrate using the pulsed laser deposition technique. The transport and photoinduced properties of the LSMO film at different annealing conditions have been investigated. The phase transition temperature decreases and the electrical resistivity of the film increases with increasing the annealing time. Photoinduced properties show that the laser induces the increases of the electrical resistivity in the metallic phase and the reduction in the insulation phase. The photoconduction （△p） increases, and then decreases with increasing the annealing time. It is found that there exists the max photoconduction about 0.013 Ωcm for the sample with the 40 minutes vacuum annealing, which is attributed to double exchange interaction.
同期刊论文项目
同项目期刊论文
Morphological evolution of the interface microstructure in the presence of bubbles during directiona
期刊信息
位置：