中文摘要：
应用电化学阻抗谱（EIS）技术以单槽和串联双槽两种方式测量了同一环氧涂层金属样品5个测试点在浸泡过程中阻抗行为的变化．通过两种测试方式中涂层金属体系各测量点的极化电阻Rp（Rp=Rc＋Rct＋Rdiff）间的关联性，说明了涂层金属的EIS双槽检测技术的可靠性．实验结果表明：同一样品两个测试点的阻抗差别较大时，采用串联双槽测量的总阻抗值与其中的高阻抗测试点的阻抗值更为接近，两个测试点单槽测量的Rp（Rc＋Rct＋Rdiff）之和（∑Rpi）与双槽测量的Rp间存在较大偏差；阻抗相近的两个测试点进行串联测量时，Rp近似等于两点分别以单槽方法所得Rp之和（∑Rpi）；两个测试点的阻抗均较小时，串联后测得的Rp与两点单独测量的Rp之和间存在较大偏差．
英文摘要：
The single- and series double-cell compartments were used to study the impedance behaviors of five sites on the epoxy-covered metal. The experimental results suggested that in the case of big difference in impedance value of two selected sites, the total impedance between the two sites obtained by double-cell method is close to that of the site with higher impedance, and the relative error between a sum of Rp of the two sites obtained by single-cell method and that obtained by double-cell method is large. If impedance values of two sites are similar, the total Rp measured by double-cell compartment almost equals to the sum of Rp obtained by single-cell method, and the relative error is small. But when both impedance values of two sites axe small, there was big relative error between Rp obtained by double-cell method and the sum of Rp measured by single-cell way on the same two sites.
同期刊论文项目
同项目期刊论文
Phenomenon of Micro-droplets Formation on Metals during the Deliquescence of Salt Particles in Atmos
Characterisation of initial atmospheric corrosion carbon steels by field exposure and laboratory sim
In situ observation of crack initiation and propagation of the charged AZ91 alloy under cyclic wet-d
The Influence of Ni alloying on Corrosion Behaviors of Low Alloy Steels under Wet-Dry Cyclic Conditi
EIS study on 2024-T3 aluminum alloy corrosion in simulated acid rain under cyclic wet-dry conditions
Effects of electrodeposition potential on the corrosion properties of bis-1,2-[triethoxysilyl] ethan
Enhancement of Corrosion Performance of Epoxy Coatings by Chemical Modification With GPTMS Silane Mo
Improving the formation and protective properties of silane films by the combined use of electrodepo
Electrochemical activity, stability and degradation characteristics of IrO2-based electrodes in aque
AC impedance spectroscopy study of the corrosion behavior of an AZ91 magnesium alloy in 0.1 M sodium
In situ observation of initial corrosion of AZ91 magnesium alloy with residual stress in cyclic wet-
Influence of Intermittent Loading on SCC Behavior for an X70 Pipeline Steel in a Near Neutral pH Sol
The cavitation erosion and erosion-corrosion behavior of carbon steel in simulating solutions of thr
Effect of passivity on electrochemical corrosion behavior of alloys during cavitation in aqueous sol
ESEM observation of the process of hydrogen generation around the micro-droplets on AZ91 magnesium a
Electrochemical measurements by a combination microelectrode in a crevice simulating disbonded coati
Electrochemical investigations of micro-droplets formed on metals during the deliquescence of salt p
In situ observation of the formation and spreading of micro-droplets on magnesium and its alloys und
Synergistic Effect of Copper and Manganese on Resistant to Atmospheric Corrosion For Low alloy steel
Investigation of stress corrosion cracking behaviors of an AZ91 magnesium alloy in 0.1kmol/m3 Na2SO4
Corrosion electrochemical characteristics of red iron oxide pigmented epoxy coatings on aluminum all
Cavitation erosion corrosion behavior of CrMnB stainless overlayer and 0Cr13Ni5Mo stainless steel in
Effect of calcination temperature on electrocatalytic activities of Ti/IrO2 electrodes in methanol a
An Enhancement of Corrosion Performance of Epoxy Coatings by Chemical Modification with GPTMS Silane
位置：