中文摘要：
采用浸渍法制备了MoO3/P25催化剂（MoO3/P25（x）,x为MoO3与P25质量比）,用X射线衍射、紫外-可见漫反射光谱、傅里叶变换红外光谱及拉曼光谱等手段对样品进行了表征,并用催化降解亚甲基蓝考察了催化剂在可见光区的催化活性.结果表明,MoO3在P25表面最大单层负载量对应的MoO3与P25质量比在0.1左右.单层分散的氧化钼物种与P25之间有较强的相互作用,降低了P25禁带宽度,提高了催化剂对可见光的吸收.当MoO3与P25质量比大于0.1时,会生成晶相MoO3,催化剂对可见光的吸收反而随MoO3担载量增加而降低.催化剂禁带宽度不是决定其可见光下催化降解亚甲基蓝活性的唯一因素.具有适宜禁带宽度和一定晶相MoO3含量的MoO3/P25（0.25）表现出最佳活性.
英文摘要：
MoO3/P25 catalysts were prepared by an impregnation method.The catalysts were characterized by X-ray diffraction,ultraviolet-visible spectrophotometry,Fourier transform infrared spectroscopy,and laser Raman spectroscopy,and their photocatalytic activty was evaluated by the degradation of methylene blue dye under visible light.The monolayer dispersion threshold of MoO3 on P25 was around 0.1 g/g.The strong interaction between the monolayer-dispersed tetrahedral-coordinated molybdenum oxide species and P25 led to a decrease in the band gap of P25,thus increasing the visible light absorption of the catalyst.Crystalline MoO3 was formed on catalysts with a MoO3/P25 mass ratio above 0.1.In these cases,the visible light absorption of the catalysts decreased with increasing MoO3 content.The band gap of the catalyst was not the only factor affecting its photocatalytic activity for the degradation of methylene blue under visible light.MoO3/P25 with the MoO3 to P25 mass ratio of 0.25,which possessed not only suitable band gap but also a certain amount of crystalline MoO3,showed the best catalytic performance.
同期刊论文项目
同项目期刊论文
Decomposition of hydrogen sulfide in non-thermal plasma aided by supported CdS and ZnS semiconductor
Decomposition of Hydrogen Sulfide in Non-Thermal Plasma Aided by Supported ZnxCd1-xS Solid Solutions
Hydrodesulfurization of 4,6-dimethyldibenzothiophene and its hydrogenated intermediates over bulk Ni
Highly acidic mesoporous aluminosilicates assembled from zeolitic subunits generated by controllable
Hydrothermalsynthesisofwell-dispersedultrafineN-dopedTiO2 nanoparticles with enhanced photocatalytic
Preparation of high-performance MoP hydrodesulfurization catalysts via a sulfidation–reduction proce
Hydrodesulfurization of dibenzothiophene catalyzed by Pd supported on overgrowth-type MCM-41/HY comp
Highly acidic mesoporous aluminosilicates prepared from preformed HY zeolite in Na2SiO3 alkaline buf
Oxidation of dibenzothiophene with cumene hydroperoxide on MoO3/SiO2
modified with alkaline earth me
Preparation of MoO3-CeO2-SiO2 Oxidative Desulfurization
Catalysts by a Sol-Gel Procedure
溶胶-凝胶法制备 Mo
Different role of H2S and dibenzothiophene in the incorporation of sulfur in the surface of bulk MoP
Synthesis of 4,6-Dimethyldibenzothiophene and 1,2,3,4-Tetrahydro-4,6-dimethyldibenzothiophene via Ti
Creation of Oxygen Vacancies in MoO3/SiO2 by Thermal Decomposition of Pre-Impregnated Citric Acid Un
Oxidative Desulfurization of Dibenzothiophene over Tungsten Oxides Supported on SiO2 and gamma-Al2O3
Hydrothermal synthesis of ionic liquid [Bmim]OH-modified TiO2 nanoparticles with enhanced photocatal
期刊信息
位置：