中文摘要：

采用改进的静电纺丝装置结合溶胶凝胶技术制备了超长的定向排列的YMnO3/PVP复合纳米纤维,将其在900℃高温煅烧6 h得到了六方相YMnO3（H YMnO3）单晶纳米纤维。用SEM,XRD,TEM,SAED及VSM对样品的相纯度,表面形貌、晶体结构和磁性能进行了表征。结果表明：YMnO3/PVP复合纳米纤维的长度可达数米,表面光滑,定向度高,形貌均一,平均直径为150-230 nm;H-YMnO3纤维的直径为70-100 nm,表面光滑呈莲藕状;在室温下的磁测量结果表明,H-YMnO3纳米纤维具有弱铁磁性。

英文摘要：

The ultralong and aligned YMnO3/PVP composite nanofibers have been synthesized by sol-gel based on modified electrospinning setup.After calcining the as-spun YMnO3/PVP fiber at 900℃for 6 h in air atmosphere,the single-crystalline hexagonal YMnO3（H-YMnO3） nanofiber can be obtained.The fabricated products were characterized by SEM,XRD,TEM,SAED and VSM to reveal the phase purity,morphologic,crystalline structure and magnetic properties.The results show that the YMnO3/PVP composite nanofibers presented smooth surface,high alignment degree and a rather uniform diameter around 150-230 nm over a length of several meters,the H-YMnO3 nanofibers exhibited lotusroot -like morphology and surface-smooth;and have a reduced diameter ranging from 70 to 100 nm. H-YMnO3 nanofibers has weak ferromagnetism at room temperature.