以聚己内酯二元醇（PCL,Mn=1000）、甲苯二异氰酸酯（TDI）和二羟甲基丙酸（DMPA）为原料,采用自乳化法制备水性聚氨酯（WPU）乳液,并用此聚氨酯乳液与聚乙烯醇（PVA）以及外加交联剂氮丙啶进行复配制得WPU/PVA复合乳液.实验研究了m（WPU）/m（PVA）对复合乳液性能及纸张表面性能的影响.研究表明,当复合乳液中WPU含量为75%,此WPU/PVA复合乳液具有优异的表面施胶性能,纸张耐折度达到1025次,干湿强度分别为162.3,57.4N,施胶度达到97s.并通过红外光谱（FT-IR）、动态激光光散射法（DLS）及热重分析（TGA）对聚合物进行了表征.
英文摘要：
The anionic waterborne polyurethane emulsion was successfully prepared by the reaction of polycapro-lactone diols (PCL),toluene diisocyanate(TDI),dimethylolpropionic acid(DMPA).A series of waterborne polyurethane/polyvinyl alcohol compound latex were synthesized by polyurethane,polyvinyl alcohol and aziri-dine as crosslinker. The results show that the compound emulsion owns excellent sizing property when m(WPU)=75%.The papers’folding endurance can reach 1 025 times,paper stiffness reach 72.1 mN,the dry and wet tensile strength respectively reach 162.3,57.4 N,sizing value reach 97 s.The polymer was character-ized with FT-IR,DLS and TG.
同期刊论文项目
同项目期刊论文
Phase behavior, interaction and properties of acetic acid lignin-containing polyurethane films coupl
The Effect of PETA/PETTA Composite System on the Performance of UV Curable Waterborne Polyurethane A
Preparation and colloidal properties of an aqueous acetic acid lignin containing polyurethane surfac
Preparation and characterization of polypyrrole/cellulose fiber conductive composites doped with cat
期刊信息
位置：