中文摘要：

运用复合激发剂活化钢渣制备复合胶凝材料，用正交实验法确定激发剂的最佳配比；研究复合胶凝材料的抗压强度等性能；确定复合激发剂的最优组合，并研究复合激发剂掺入量对材料抗压强度的影响，结果显示复合激发剂最佳质量掺入量为3％；分析材料3d、28d的水化矿物，结果表明，复合激发剂可激发制得净浆3d抗压强度28MPa、28d抗压强度45MPa的复合胶凝材料；微观分析显示，水化初期矿物以氢氧化钙和钙矾石为主，水化28d生成大量的C-S-H凝胶，复合水泥强度大幅提高。

英文摘要：

Using chemical activator to improve activity of steel slag cement. It is put forward the best ratio of different activators. The compressive strength of 3 d and 28 d of cements was tested. The hydration mineral of different days was analysed. It shows that compound activator can improve activity of cement, and the compressive Strength of 3 d receive 28 MPa. There are many Biocalc and AFt at initial stage. In 28 d, more C-S-H were produced and the strength improved greatly.