中文摘要：
考察了高活性混合稀土（RE）掺杂的WC-8％Co-0．07％RE（质量分数）硬质合金刀片对铸铁的切削试验。采用扫描电镜、能谱分析以及X射线衍射等分析方法对硬质合金烧结体表面、切削试验后刀片的前刀面、后刀面以及切削刃进行观察与分析。结果表明，在稀土硬质合金刀片切削过程中发生了La、Ce从合金内部至刀片工作表面的非同步迁移现象，在刀具工作表面原位形成了具有自润滑功能的稀上氧硫化物。在实验观察与分析基础上，对La、Ce的定向迁移机制与稀土氧硫化物的形成机制进行了探讨。
英文摘要：
As-sintered high activity mischmetal （RE, with lanthanum and cerium） doped WC-8%Co-0.07%RE （mass fraction） cemented carbide inserts were tested for the turning of cast iron. The sinter skin, flank face, rake face and cutting edge of the inserts after testing were observed and analyzed by scanning electron microscopy, energy dispersive X-ray spectroscopy and X-ray diffractometry. Asynchronous migration phenomenon of lanthanum and cerium from the inside to the working faces of the as-sintered insert during the turning process was observed. The results show that a rare earth oxysulfide phase with self lubricating function forms in-situ on the working faces of cemented carbide cutting tool. The mechanisms for the directional migration and formation of rare earth oxysulfide were discussed.
同期刊论文项目
同项目期刊论文
Effect of strain rate on the compressive behaviour of a Zr56Al10.9Ni4.6Cu27.8Nb0.7 bulk metallic gla
Conversion of natural egg-shell to 3D flower-like hydroxyapatite agglomerates for highly sensitive d
Sea cucumber-like hydroxyapatite: cation exchange membrane-assisted synthesis and its application in
In situ formation of La containing dispersed phase on the sinter skin of La2O3 and Cr3C2 unitedly do
Influence of copper content on the microstructure and hardness of copperdoped tungsten carbide-cobal
Low-temperature growth of tetragonal tungsten nanowire arrays on tungsten substrate using Ni solid c
Ultrafine and nano scaled tungsten carbide synthesis from colloidal carbon coated nano tungsten prec
Directional migration behavior of cerium during the sintering process of mischmetal doped cemented c
Surface adsorption phenomenon during the preparation process of nano WC and ultrafine cemented carbi
期刊信息
位置：