中文摘要：

Chemical vapor deposition (CVD) diamond coated drills are fabricated by depositing diamond films on Co-cemented tungsten carbide (WC-Co) drills. The characteristics of as-deposited diamond coatings are investigated by scanning electron microscope (SEM) and Raman spectra. To evaluate the cutting performance of diamond coated drills, comparative drilling tests are conducted using diamond coated and uncoated WC-Co drills, with carbon fiber reinforced plastics (CFRPs) as the workpiece on a high-speed computer numerical control (CNC) machine. Thrust force and tool wear are measured during the drilling process. The results show that diamond coated drill exhibits better cutting performance, compared with the uncoated drill. The value of flank wear is about 70 μm after machining 90 holes, about a half of that of the WC-Co drill with 145 μm after drilling only 30 holes. The wear rate of WC-Co drill is higher than that of diamond coated drill before diamond films peeling off. The diamond coated drill achieves more predictable hole quality. The improved cutting performance of the diamond coated drill is due to the high hardness, wear resistance and low coefficient of friction.

英文摘要：

Chemical vapor deposition （CVD） diamond coated drills are fabricated by depositing diamond films on Co-cemented tungsten carbide （WC-Co） drills. The characteristics of as-deposited diamond coatings are in- vestigated by scanning electron microscope （SEM） and Raman spectra. To evaluate the cutting performance of diamond coated drills, comparative drilling tests are conducted using diamond coated and uncoated WC-Co drills, with carbon fiber reinforced plastics （CFRPs） as the workpiece on a high-speed computer numerical control （CNC） machine. Thrust force and tool wear are measured during the drilling process. The results show that diamond coated drill exhibits better cutting performance, compared with the uncoated drill. The value of flank wear is about 70 ~m after machining 90 holes, about a half of that of the WC-Co drill with 145 ~m after drilling only 30 holes. The wear rate of WC-Co drill is higher than that of diamond coated drill before diamond films peeling off. The diamond coated drill achieves more predictable hole quality. The improved cutting performance of the diamond coated drill is due to the high hardness, wear resistance and low coefficient of friction.