中文摘要：
采用干压成型法，通过添加适量的金属～粉来增韧Al2O3多孔支撑体，详细考察了热处理温度对多孔Al2O3／Al支撑体力学性能的影响，并借助于扫描电子显微镜（SEM）分析了样品的微观结构．研究结果表明：当热处理温度较低时，支撑体内部大量未氧化的铝相是支撑体断裂韧性提高的主要的原因；当热处理温度较高时，铝氧化产生体积膨胀，膨胀裂纹对支撑体断裂韧性的提高贡献很大．
英文摘要：
An amount of Al powder was added to toughen Al2O3 porous supports by dry press forming. Based on the toughening mechanism of Al2Oa/Al composite, the effects of heating temperature on the fracture toughness and bending strength of macroporous Al2O3/Al supports were investigated in detail, and the microstructure of specimens made of the supports was analyzed by SEM. The results show that the fracture toughness of the supports is influenced by calcining temperature. When the calcining temperature is low, unoxidized Al phase can absorb amount of fracture energy to make the fracture toughness of the supports high. But when the temperature is above 1200 ℃, the cracks which is occurred in the oxidation processing of Al phase can improve the fracture toughness of the supports, and the contribution of cracks is more important than the amount of Al phase to the fracture toughness of supports.
同期刊论文项目
同项目期刊论文
Preparation of Pd-B/TiO2 amorphous alloy catalysts and their performance on liquid-phase hydrogenati
The oxidative stream reforming of methane to syngas in a thin tubular mixed-conducting membrane reac
A new route for the fabrication of TiO2 ultrafiltration membranes with suspension derived from a wet
A novel route to synthesize nano-crystalline Ba0.5Sr0.5Co0.8Fe0.2O3?δ perovskite oxide at high tempe
Polydimethylsiloxane (PDMS)/ceramic composite membrane with high flux for pervaporation of ethanol-w
Chemical expansion, crystal structural stability, and oxygen permeability of SrCo0.4Fe0.6-xAlxO3?δ o
Organic–inorganic composite pervaporation membranes prepared by self-assembly of polyelectrolyte mul
Improving performance of a dense membrane reactor for thermal decomposition of CO2 via surface modif
Synthesis of nanocrystalline conducting composite oxides based on a non-ion selective combined compl
Match of thermal performances between the membrane and the support for supported dense mixed-conduct
A self-catalytic mixed-conducting membrane reactor for effective production of hydrogen from methane
Modeling of relationship between water permeability and microstructure parameters of ceramic membran
位置：