中文摘要：
研究激光熔化沉积Ti-6Al—2Zr-Mo-V合金在高周疲劳失效中的变形行为，并提出相应的变形机制。结果表明，激光沉积钛合金疲劳裂纹萌生和扩展中的变形行为都与其位错运动和滑移行为密切相关。疲劳裂纹扩展中的滑移主要沿两个滑移面进行；裂纹扩展亚表面存在大量二次裂纹。解释两种不同类型二次裂纹的形成机制和作用。分析粗大柱状晶晶界变形特征。
英文摘要：
Deformation behavior in high-frequency fatigue failure of laser melting deposited Ti-6Al-2Zr-Mo-V alloys was investigated. The deformation modes and mechanisms were also discussed. The results indicate that the deformation behavior during fatigue crack nucleation and propagation are closely related to the dislocation motion and slip behavior. The fatigue cracks by slip deformation propagate along two slip planes. A lot of secondary cracks were observed on the crack propagation subsurface. Formation mechanism and effect of two types of secondary cracks were explained. Grain boundary deformation of coarse-columnar crystal was also discussed.
同期刊论文项目
同项目期刊论文
Microstructure and hot corrosion behaviors of a gamma-toughened Cr13Ni5Si2/Cr3Ni5Si2 ternary metal s
Hot corrosion behaviors of a Cr13Ni5Si2-based metal silicide alloy in Na2SO4+25 wt.% K2SO4 and Na2SO
Microstructure and mechanical properties of rapid directionally solidified Ni-base superalloy Rene'4
High temperature mechanical properties of a laser melting deposited TiC/TA15 titanium matrix composi
Deformation Behavior in High-Frequency Fatigue Failure of Laser Melting Deposited Ti-6Al-2Zr-Mo-V Al
Microstructure and Tribological Property of Laser Melt Deposited alpha/Fe9Cr9Si2 Metal Silicide Allo
Effect of Annealing Temperatures on Microstructure and Mechanical Properties of Laser Melting Deposi
Microstructure and mechanical properties of directional rapidly solidified Ni-base superalloy Rene95
Microstructure and electrochemical characterization of laser melt-deposited Ti2Ni3Si/NiTi intermetal
Corrosion behaviors of a gamma-toughened Cr13Ni5Si2/Cr3Ni5Si2 multi-phase ternary metal silicide all
CORROSION BEHAVIORS OF Ni BASE SOLID SOLUTION-TOUGHENED Cr13Ni5Si2 ALLOY IN Cl- CONTAINING SOLUTIONS
Microstructure and dry sliding wear resistance of laser clad TiC reinforced Ti-Ni-Si intermetallic c
Microstructural characterization and dry sliding wear resistance of MoO2-strengthened gamma/NiMo all
Microstructure and tensile properties of laser melting deposited TiC/TA15 titanium matrix composites
Solidification microstructure and mechanical properties of corrosion-resistant ultrahigh strength st
Influence of Ni content on the microstructure and dry sliding wear properties of Cr13Ni5Si2/gamma in
Microstructure and wear resistance of laser melted Ti5Si3-TiCo-Ti2Co multiphase intermetallic alloys
期刊信息
位置：