中文摘要：

研究Ni-Al-Fe系中B2型金属间化合物NiAl（Fe）的硬度随时效时间的变化，同时测定时效处理后含析出相的NiAl（Fe）金属间化合物的屈服强度随温度变化。结果表明，在所有实验温度区域内，NiAl（Fe）化合物的屈服强度均远高于单相NiAl；析出相为体心立方结构的α-Fe相；在时效初期α-Fe相呈球状，过时效之后变成平行于有序基体〈100）晶面的板条状。通过透射电镜观察还确定变形过程中位错滑移矢量为〈111〉。虽然α-Fe析出相的硬度低于NiAl（Fe）基体，但由于α-Fe析出相对运动位错有较强的钉扎作用而使基体得到强化。

英文摘要：

Changes of hardness of B2-NiAI（Fe） intermetallic compounds in Ni-Al-Fe system with aging time and changes of yield strength of aged B2-NiAl（Fe） intermetallic compounds containing α-Fe precipitates with temperatures were investigated. Results show that the yield strength of B2-NiAl（Fe） intermetallic compounds containing α-Fe precipitates is higher than that of single phase NiAI at all the testing temperatures. It is revealed that the precipitates are disordered bc.c Fe phase. The shape of α-Fe precipitates is sphericity and keeps coherent with the matrix in the initial aging period. With prolonging the aging time, the precipitates are platelet in shape, nearly parallel to the {100} planes of the B2-ordered matrix. TEM observation determines that the Burgers vector of the slipping dislocation is 〈111〉. Although the hardness of α-Fe precipitates is lower than that of B2-NiAl（Fe） matrix, the pinning effect of the a-Fe precipitates on moving dislocation plays an important role in hardening of the B2-NiAl（Fe） matrix.