中文摘要：
研究矿物掺合料、钢纤维及试件尺寸对水泥基材料抗压与抗折强度的影响规律.试验结果表明：矿物掺合料提高水泥基材料28 d抗折强度,但降低其早期抗压强度;掺粉煤灰或硅粉对水泥基材料抗压强度影响较小;掺2%钢纤维水泥基材料抗压强度提高30-50 MPa,抗折强度增加1倍以上,28 d抗压强度接近100 MPa,抗折强度达到22-32MPa.将试件尺寸由40 mm×40 mm×160 mm提高到100 mm×100 mm×100 mm,其抗压强度大幅度降低.
英文摘要：
Mineral admixtures, steel fiber and specimen size on compressive and flexural strength of the material were studied. The result shows that 28 d flexural strength of cement-based materials with mineral admixture were improved but early compressive strength reduced; and the content of fly ash or silica fume shows little influence on it. Mixed with 2% steel fibers, the compressive strength of cement-based materials were improved by 30 - 50 MPa, flexural strength more than doubled, 28 d compressive strength of cement-based materials closed to 100 MPa, flexural strength were increased to 22 × 32 MPa. The specimen size of 40 mm ×40 mm ×160 mm increased to 100 mm ×100 mm × 100 mm, a significant reduction on comoressive strength values.
同期刊论文项目
同项目期刊论文
Damage of cement paste in sulfate environment with different temperature and drying-immersion cycles
Corrosive Crack and its 3D Defects Identification of Reinforced Concrete Subjected to Coupled Effect
Aqueous processing and effects of V2O5 on microwave dielectric properties of multilayer Li1.075Nb0.6
期刊信息
位置：