中文摘要：

Cr^2＋：ZnSe具有很宽的吸收带和发射带，是中红外波段优秀的可调谐激光材料。从吸收光谱、发射光谱以及角度调谐输出对Cr^2＋：ZnSe晶体的激光输出性能进行了研究。采用真空高温扩散法制备Cr^2＋：ZnSe晶体，获得了高浓度的Cr^2-离子掺杂的厚1．7mm，直径10mm的薄片ZnSe晶体。使用中心波长2．05μm，最大输出功率8W的Tm离子掺杂的光纤激光器抽运，使用平凹腔结构搭建谐振腔，获得了最大平均功率1．034W，中心波长2．367μm，线宽10nm的连续激光输出。利用角度调谐的方法，对Cr：ZnSe晶体的调谐性能进行了研究，在100nm范围内获得了调谐输出。

英文摘要：

Cr^2＋ ：ZnSe having a wide range of absorption and emission spectra, is an excellent tuning laser material in mid-IR wavelength range. In this paper, lasing abilities of Cr^2＋ ：ZnSe had been studied by analyzing the absorption spectrum, emission spectrum and tuning ability. The Cr^2＋ ：ZnSe poly-crystal laser material is prepared by physical vapour transport （PVT） technique. The sample is cut and polished in thickness of 1.7 mm and with diameter of 10 mm. Pumped by a 2.05 μm Tm-ion doped silica fiber laser, delivering maximum output power of 8 W, maximum average output power of 1. 034 W around 2. 367 μm was demonstrated in a plate- concave resonate. The laser bandwidth was measured as 10 nm. At the same time, the laser can be tuned in 100 nm range by angle-tuning method in research of tuning ability of the laser material.