中文摘要：
利用溶液滴膜的方法在云母表面制备聚苯乙烯一聚异戊二烯一聚苯乙烯（SIS）三嵌段共聚物薄膜，用原子力显微镜（AFM）观察其表面形态．发现共聚物经微相分离，在薄膜中形成平行于表面的条纹形态，相周期约（38±5）nm，并且观察到条纹环绕形成的螺旋图案，图案尺寸超过1μm．在螺旋中心某一组分形成闭合端，而其它区域条状相沿螺旋切线方向平行排列．嵌段共聚物溶液成膜过程中，螺旋图案的产生是由于微相分离过程耦合流体力学相互作用产生的不稳定性所导致．
英文摘要：
Polystyrene-polyisoprene-polystyrene （SIS） triblock copolymer thin film was prepared by solution casting on the freshly cleaved mica surface. The film was then directly scanned using atomic force microscopy （AFM）. It was observed that the copolymer microphase separated into stripe structure mostly parallel to the film surface with a period of 38 ± 5 nm. A spiral structure with a diameter of more than 1 μm was circulated by the stripes. A closed end was formed with one of the components in the center of the spiral, and away from the spiral center the stripes bent along the tangent of the spiral. The occurrence of the spiral is due to the instability caused by the block copolymer microphase separation coupled with the hydrodynamic effect during the course of the film formation.
同期刊论文项目
同项目期刊论文
Synthesis of polymer grafted carbon nanotubes by nitroxide mediated radical polymerization in the pr
A Discrete, Space Variation Model for Studying the Kinetics of Shape Deformation of Vesicles Coupled
Self-assembled pattern formation of block copolymers on the surface of the sphere using self-consist
Kinetic analysis of the cross reaction between dithioester and alkoxyamine by a Monte Carlo simulati
Cylindrical phase of diblock copolymers confined in thin films A real-space self-consistent field th
Two-dimensional infrared correlation spectroscopy as a probe of sequential events in the diffusion p
Aggregate morphologies of amphiphilic ABC triblock copolymer in dilute solution using self-consisten
Novel synthesis of highly branched comb-like polymers by coupling reaction of polystyryllithium with
Effects of reversible chemical reaction on morphology and domain growth of phase separating binary m
Threading-unthreading equilibrium in solution of molecular nanotubes and linear flexible polymer cha
位置：