中文摘要：

对L3纯Al进行了Ti离子注入与阳极氧化，用X射线光电子能谱仪（XPS）分析了阳极氧化膜层的表面成分，利用电化学阻抗谱（EIS）研究了阳极氧化膜的腐蚀行为，结果表明，Ti离子以TiO2的形式存在于Al阳极氧化膜层中，Ti离子的注入并不影响Al阳极氧化膜的非晶结构，Ti离子注入可以使Al阳极氧化膜在酸性和碱性的NaCl溶液中的阻抗参数R明显提高，参数C降低。

英文摘要：

Commercial pure aluminum L3 was implanted by Ti ions and then anodic oxidation was carried out. Electrochemical impedance spectroscopy （EIS） and XPS were used to study the influences of Ti ion implantation on corrosion behavior of anodic oxide film in NaC1 solution. XPS analysis revealed that Ti is present in the anodic film as TiO2. XRD proved that Ti ions implantation does not change the amorphous structure of the film. EIS showed that the implantation can improve the corrosion resistance of the anodic oxide films in acidic and basic solutions, and the parameters R and C in EIS increased and decreased, respectively.