中文摘要：
根据C／SiC复合材料的结构以及等温化学气相浸渗法的工艺特点，建立了ICVI过程中C纤维预制体结构变化的多尺度孔隙模型和C／SiC复合材料ICVI致密化过程的数学模型．利用该模型对ICVI法制备C／SiC复合材料进行了数值计算和分析．模拟结果与实验结果呈现出相同的规律并且两者之间误差较小，表明本文所建立的模型可以很好地描述C／SiC复合材料的ICVI致密化过程．利用该模型计算出C／SiC复合材料孔隙率的分布情况以及总体孔隙率在浸渗过程中的演化规律，对ICVI工艺的优化具有一定的指导意义.
英文摘要：
The multi-scale porosity model depicting infiltration induced changes of carbon fiber preform and the mathematical model depicting ICVI process for fabrication of C/SiC composites were developed. The integrated model was proposed to simulate densification behavior of C/SiC composites. The correspondences of calculation results and the experimental data indicate that the model is reasonable and feasible to characterize ICVI process of C/SiC composites. The calculated results, such as distribution of local porosity, uniformity of densification and evolution of global porosity during infiltration process, lay foundation of further research and optimization of ICVI process for fabrication of C/SiC composites.
同期刊论文项目
同项目期刊论文
Nondestructive evaluation and mechanical characterization of a defect-embedded ceramic matrix compos
Behavior of two-dimensional C/SiC composites subjected to thermal cycling in controlled environments
The Acoustic Emission Characteristics of Silicon Carbide Firber Reinforced composite Under Tensile L
Acoustic Emission Research on Thermal Shock Behaviors of Three-Dimensional C/SiC Composites in Diffe
Damage analysis of 2D C/SiC composites subjected to thermal cycling in oxidizing environments by mec
Thermal expansion behavior of carbon fiber reinforced chemical-vapor-infiltrated silicon carbide com
Thermal cycling response behavior of ceramic matrix composites under load and displacement constrain
Damage mechanisms of C/SiC composites subjected to constant load and thermal cycling in oxidizing at
Effect of shrinkage constraint on damage of C/SiC composites during thermal cycles in oxidising atmo
Numerical Simulation of Effect of Methyltrichlorosilane Flux on Isothermal Chemical Vapor Infiltrati
Thermal cycling damage mechanisms of C/SiC composites in displacement constraint and oxidizing atmos
Comparative Modeling of Gas Transport in Isothermal Chemical Vapor Infiltration Process of C/SiC Com
Modeling the effects of thermal and mechanical load cycling on a C/SiC composite in oxygen/argon mix
Relationship of damage evolution of ceramic matrix composites between static and dynamic oxidizing g
Residual strength prediction of SiC/SiC composite exposed to service environments with factor analys
Monotonic tensile behavior analysis of three-dimentional needle-punched Wover C/SiC Composites by Ac
Life Prediction of 3D woven C/SiC Composites at High Temperatures with Low Frequency Cyclic Stresses
Experimental research on failure mechanism of a CVI-fabricated ceramic matrix composite under compre
Tension-tension fatigue damage characteristics of a 3D SiC/SiC composite in H2O-O2-Ar environment at
Oxidation protective multilayer CVD SiC coatings modified by a graphitic B-C interlayer for 3D C/SiC
Characterization of tensile behavior of a two-dimensional woven carbon/silicon carbide composite fab
Stress-Oxidationbehavior of a carbon/silicon carbide composite in a high temperature combustion envi
Tensile behavior and microstructural evolution of a carbon/silicon carbide composite in simulated re
Effect of temperature gradients and stress levels on damage of C/SiC composites in oxidizing atmosph
Experimental simulation of the space re-entry environment for a carbon/silicon carbide composite and
位置：