中文摘要：

采用固相反应法制备了Y掺杂（Ba0.6Sr0.3Ca0.1）1-xYxTi0.999Mn0.001O3（0≤x≤0.007）陶瓷,重点研究了Y含量对BSCT基陶瓷的显微结构、介电性能和热释电性能的影响。结果表明：随着Y含量的增加,BSCYxTM陶瓷的平均晶粒尺寸逐渐减小,介电常数、介电损耗、居里温度和热释电系数均呈现先增加后减小的趋势。当Y掺杂量为0.7mol%时,BSCYxTM陶瓷的平均晶粒尺寸最小为3.1μm,且探测优值Fd较大,最大值可达8.22×10-5Pa-1/2（700 V/mm,30℃）,高于采用溶胶-凝胶法制备的同组分陶瓷的探测优值5.91×10-5Pa-1/2。

英文摘要：

（Ba0.6Sr0.3Ca0.1）1-xYx Ti0.999Mn0.001O3（0≤x≤0.007） ceramics were prepared by the solid-state reaction technique.The effects of Y doping on the microstructure,dielectric properties and pyroelectric properties were investigated.The average grain size decreases with the increase of Y concentration.The dielectric and pyroelectric properties measurement results show that the dielectric constant,dielectric loss,T c and pyroelectric coefficient all initially increase and then decrease with Y concentration.And the pyroelectric figure of merit F d can be improved by the Y doping.The specimen doped with 0.7mol%Y shows a higher maximum F d value of 8.22×10-5 Pa-1/2 under 700 V/mm near 30℃ with the smallest average grain size of 3.1 μm,indicating its promising application in infrared thermal imaging arrays devices.