中文摘要：
采用化学气相渗透法（CVI）制备了二维炭纤维增强碳化硅（C/SiC）全陶瓷基复合材料铰链试样.高温燃气风洞实现了铰链试样在1800℃高温氧化气氛中传动与摩擦行为的试验模拟.基于耦合应力等效模拟系统的开发,采用摩擦力矩的变化表征材料的传动与摩擦行为.对比分析了材料在室温与高温下以传动为背景的高载荷、低转速摩擦磨损行为及机理.C/SiC复合材料铰链试样在高温燃气环境中稳定的摩擦力矩和对滑动时间的不敏感,验证了材料在高温下更稳定、更可靠的高温摩擦性能及热承载能力.高温下表面生成的氧化反应膜通过应力的重新分布起到有效的保护与润滑作用.
英文摘要：
An all-ceramic hinge based on the two dimensional carbon fiber reinforced silicon carbide matrix （C/SiC） composites was prepared by chemical vapor infiltration. The high temperature combustion wind tunnel realized simulation of the transmitting and friction behavior of the hinge at 1800℃ in an oxidizing atmosphere. Based on the coupling stress equivalent simulation system, a characterization method with the change of torque was proposed to evaluate the friction behavior. The friction and wear behavior as well as wear mechanism were studied both at high temperatures in combustion environment and at room temperature in air. The results indicate that the friction torque is stable and insensitive to the sliding time at high temperatures, which demonstrates stable and reliable friction property and thermal load-carrying ability of the hinge. The tribochemical reaction products on contact surface may moderate the stress distribution by providing a reaction layer for wear protection and lubrication.
同期刊论文项目
同项目期刊论文
Nondestructive evaluation and mechanical characterization of a defect-embedded ceramic matrix compos
Behavior of two-dimensional C/SiC composites subjected to thermal cycling in controlled environments
The Acoustic Emission Characteristics of Silicon Carbide Firber Reinforced composite Under Tensile L
Acoustic Emission Research on Thermal Shock Behaviors of Three-Dimensional C/SiC Composites in Diffe
Damage analysis of 2D C/SiC composites subjected to thermal cycling in oxidizing environments by mec
Thermal expansion behavior of carbon fiber reinforced chemical-vapor-infiltrated silicon carbide com
Thermal cycling response behavior of ceramic matrix composites under load and displacement constrain
Damage mechanisms of C/SiC composites subjected to constant load and thermal cycling in oxidizing at
Effect of shrinkage constraint on damage of C/SiC composites during thermal cycles in oxidising atmo
Numerical Simulation of Effect of Methyltrichlorosilane Flux on Isothermal Chemical Vapor Infiltrati
Thermal cycling damage mechanisms of C/SiC composites in displacement constraint and oxidizing atmos
Comparative Modeling of Gas Transport in Isothermal Chemical Vapor Infiltration Process of C/SiC Com
Modeling the effects of thermal and mechanical load cycling on a C/SiC composite in oxygen/argon mix
Relationship of damage evolution of ceramic matrix composites between static and dynamic oxidizing g
Residual strength prediction of SiC/SiC composite exposed to service environments with factor analys
Monotonic tensile behavior analysis of three-dimentional needle-punched Wover C/SiC Composites by Ac
Life Prediction of 3D woven C/SiC Composites at High Temperatures with Low Frequency Cyclic Stresses
Experimental research on failure mechanism of a CVI-fabricated ceramic matrix composite under compre
Tension-tension fatigue damage characteristics of a 3D SiC/SiC composite in H2O-O2-Ar environment at
Oxidation protective multilayer CVD SiC coatings modified by a graphitic B-C interlayer for 3D C/SiC
Characterization of tensile behavior of a two-dimensional woven carbon/silicon carbide composite fab
Stress-Oxidationbehavior of a carbon/silicon carbide composite in a high temperature combustion envi
Tensile behavior and microstructural evolution of a carbon/silicon carbide composite in simulated re
Effect of temperature gradients and stress levels on damage of C/SiC composites in oxidizing atmosph
Experimental simulation of the space re-entry environment for a carbon/silicon carbide composite and
期刊信息
位置：