中文摘要：

In this paper, the serpentine channel pouring process for preparing a semi-solid A390 alloy slurry and refining the primary Si grains of the A390 alloy, was used. The effects of the pouring temperature, the cooling water flow and the number of the curves on the size of the primary Si grains in the semi-solid A390 alloy slurry were investigated. The results show that the pouring temperature, the cooling water flow and the number of the curves have a major effect on the size and the distribution of primary Si grains. Under the experimental condition of the four-curve copper channel whose cooling water flow was 500 L·h-1 and the pouring temperature was 690 oC, the primary Si grains of the semi-solid A390 alloy slurry were refined to the greatest extent and the lath-like grains were changed into granular ones. Additionally, the equivalent grain diameter and the average shape factor of the primary Si grains of the satisfactory semi-solid A390 alloy slurry are 18.6 μm and 0.8, respectively. Further, the refinement mechanism of the primary Si grains through the serpentine channel pouring process was analyzed and discussed. In summary, the primary Si nuclei could be easily precipitated due to the chilling effect of the channel inner wall, thus the primary Si grains were greatly refined. Meanwhile, the subsequent alloy melt fluid also promoted the separation of primary Si grains from the inner wall, further refining the primary Si grains.

英文摘要：

In this paper, the serpentine channel pouring process for preparing a semi-solid A390 alloy slurry and refining the primary Si grains of the A390 alloy, was used. The effects of the pouring temperature, the cooling water flow and the number of the curves on the size of the primary Si grains in the semi-solid A390 alloy slurry were investigated. The results show that the pouring temperature, the cooling water flow and the number of the curves have a major effect on the size and the distribution of primary Si grains. Under the experimental condition of the four-curve copper channel whose cooling water flow was 500 L·h-1 and the pouring temperature was 690 oC, the primary Si grains of the semi-solid A390 alloy slurry were refined to the greatest extent and the lath-like grains were changed into granular ones. Additionally, the equivalent grain diameter and the average shape factor of the primary Si grains of the satisfactory semi-solid A390 alloy slurry are 18.6 μm and 0.8, respectively. Further, the refinement mechanism of the primary Si grains through the serpentine channel pouring process was analyzed and discussed. In summary, the primary Si nuclei could be easily precipitated due to the chilling effect of the channel inner wall, thus the primary Si grains were greatly refined. Meanwhile, the subsequent alloy melt fluid also promoted the separation of primary Si grains from the inner wall, further refining the primary Si grains.